Copper Alloy C28000 vs C41300
Copper Alloy · grade comparison
Copper Alloy C28000 and C41300 are both copper alloy grades. C41300 is the stronger of the two: yield strength 400 MPa (58 ksi) against 145 MPa (21 ksi) for C28000, about 176% more; tensile strength follows at 455 MPa (66 ksi) vs 372 MPa (54 ksi). In exchange, C28000 is the more ductile: elongation 45% versus 8% for C41300, and C41300 is harder (130 HB vs 75 HB). C28000 is lighter (8.39 g/cm³ vs 8.8 g/cm³ for C41300) and C28000 runs hotter in service (200°C vs 180°C continuous). On the shop floor, C28000 machines more easily (good vs poor) and C28000 sits in a lower cost tier (premium, $$$) than C41300 (high, $$$$).
C28000Choose it when the part is bent, formed or impact-loaded, or when weight is the constraint.
C41300Choose it when strength drives the design.
C28000 vs C41300: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Poisson's Ratio 0.34
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Min Service Temperature
Electrical
Conductivity and insulation.
Electrical Resistivity
Same in both: Electrical Conductivity 28 % IACS
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.28 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Castability
Brazeability / Solderability
Polishability
Same in both: Formability (cold) 55 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Same in both: Specific Stiffness (E / density) 12.5 MN·m/kg
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | C28000 | C41300 |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Default condition | O | — |
| Relative cost | $$$ Premium | $$$$ High |
| Min. machined wall | 0.8 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| Chrome Plating | Yes | — |
| Electropolishing | Yes | — |
| Nickel Plating | Yes | — |
| Painting | Yes | — |
| Tin Plating | Yes | — |
They share 4 finishes: Copper Plating, Electroless Nickel (EN), Gold Plating, Silver Plating.
C28000 vs C41300 — frequently asked
Is C41300 stronger than C28000?
Yes. C41300 has a typical yield strength of 400 MPa (58 ksi) against 145 MPa (21 ksi) for C28000 — about 176% more. Tensile strength is 455 MPa (66 ksi) vs 372 MPa (54 ksi).
Which is cheaper, C28000 or C41300?
C28000 is the lower-cost material: it sits in the premium tier ($$$) while C41300 is high ($$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, C28000 or C41300?
C28000. Its machinability rates good (55/100) against poor (30/100) for C41300; for welding the order is C41300 first (good, 55/100) then C28000 (fair, 50/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in C28000 and C41300 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.