Copper Alloy C28000 vs C32000
Copper Alloy · grade comparison
Copper Alloy C28000 and C32000 are both copper alloy grades. C32000 is the stronger of the two: yield strength 270 MPa (39.2 ksi) against 145 MPa (21 ksi) for C28000, about 86% more. In exchange, C28000 is the more ductile: elongation 45% versus 25% for C32000, and C32000 is harder (100 HB vs 75 HB). C28000 is lighter (8.39 g/cm³ vs 8.75 g/cm³ for C32000) and C32000 is stiffer (117 GPa vs 105 GPa). On the shop floor, C32000 machines more easily (very good vs good), C28000 welds better (fair vs poor), and C28000 sits in a lower cost tier (premium, $$$) than C32000 (high, $$$$).
C28000Choose it when the part is bent, formed or impact-loaded, or when weight is the constraint.
C32000Choose it when strength drives the design, or when the part is machined in volume.
C28000 vs C32000: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Same in both: Poisson's Ratio 0.34
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Min Service Temperature
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Castability
Brazeability / Solderability
Polishability
Same in both: Formability (cold) 55 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | C28000 | C32000 |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Default condition | O | — |
| Relative cost | $$$ Premium | $$$$ High |
| Min. machined wall | 0.8 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| Chrome Plating | Yes | — |
| Electropolishing | Yes | — |
| Nickel Plating | Yes | — |
| Painting | Yes | — |
| Tin Plating | Yes | — |
They share 4 finishes: Copper Plating, Electroless Nickel (EN), Gold Plating, Silver Plating.
C28000 vs C32000 — frequently asked
Is C32000 stronger than C28000?
Yes. C32000 has a typical yield strength of 270 MPa (39.2 ksi) against 145 MPa (21 ksi) for C28000 — about 86% more. Tensile strength is 350 MPa (50.8 ksi) vs 372 MPa (54 ksi).
Which is cheaper, C28000 or C32000?
C28000 is the lower-cost material: it sits in the premium tier ($$$) while C32000 is high ($$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, C28000 or C32000?
C32000. Its machinability rates very good (80/100) against good (55/100) for C28000; for welding the order is C28000 first (fair, 50/100) then C32000 (poor, 20/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in C28000 and C32000 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.