Copper Alloy C26000 vs C26200
Copper Alloy · grade comparison
Copper Alloy C26000 and C26200 are both copper alloy grades. C26200 is the stronger of the two: yield strength 379 MPa (55 ksi) against 105 MPa (15.2 ksi) for C26000, about 3.6 times as much; tensile strength follows at 490 MPa (71.1 ksi) vs 325 MPa (47.1 ksi). In exchange, C26000 is the more ductile: elongation 62% versus 23% for C26200, and C26200 is harder (125 HB vs 55 HB).
C26000Choose it when the part is bent, formed or impact-loaded.
C26200Choose it when strength drives the design.
C26000 vs C26200: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Vickers
Hardness, Rockwell B
Same in both: Elastic (Young's) Modulus 110 GPa16 Msi · Shear Modulus 41 GPa5.9 Msi · Bulk Modulus 115 GPa16.7 Msi
Physical
Density and transition temperatures.
Density
Same in both: Melting Point (Solidus) 915°C1,679 °F · Liquidus Temperature 955°C1,751 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Latent Heat of Fusion
Same in both: Specific Heat Capacity 375 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 19.9 µm/m·K11.1 µin/in·°F · Max Service Temperature (continuous) 200°C392 °F · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 28 % IACS · Electrical Resistivity 6.2×10⁻⁸ Ω·m2.44 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Formability (cold)
Castability
Same in both: Machinability Rating (AISI 1212 = 100 %) 30% · Weldability 40 / 100 · Brazeability / Solderability 90 / 100 · Polishability 85 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Same in both: Specific Stiffness (E / density) 12.9 MN·m/kg
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | C26000 | C26200 |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Default condition | O | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | 0.8 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| Chrome Plating | Yes | — |
| Electropolishing | Yes | — |
| Nickel Plating | Yes | — |
| Painting | Yes | — |
| Tin Plating | Yes | — |
They share 4 finishes: Copper Plating, Electroless Nickel (EN), Gold Plating, Silver Plating.
C26000 vs C26200 — frequently asked
Is C26200 stronger than C26000?
Yes. C26200 has a typical yield strength of 379 MPa (55 ksi) against 105 MPa (15.2 ksi) for C26000 — about 3.6 times as much. Tensile strength is 490 MPa (71.1 ksi) vs 325 MPa (47.1 ksi).
Which is cheaper, C26000 or C26200?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
When should I choose C26000 over C26200?
Pick C26000 when the part is bent, formed or impact-loaded. Pick C26200 when strength drives the design.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C26000 and C26200 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.