Copper Alloy C26000 vs C68300
Copper Alloy · grade comparison
Copper Alloy C26000 and C68300 are both copper alloy grades. Both yield at about 105 MPa — strength does not separate them. C26000 is the more ductile: elongation 62% versus 55% for C68300, and C68300 is harder (58 HB vs 55 HB). On the shop floor, C68300 welds better (good vs fair).
C26000Choose it when the part is bent, formed or impact-loaded.
C68300Choose it when it will be welded.
C26000 vs C68300: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Poisson's Ratio
Tensile Strength (Ultimate)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Vickers
Charpy V-Notch Impact (RT)
Hardness, Rockwell B
Same in both: Elastic (Young's) Modulus 110 GPa16 Msi · Shear Modulus 41 GPa5.9 Msi · Bulk Modulus 115 GPa16.7 Msi · Yield Strength (0.2% offset) 105 MPa15.2 ksi
Physical
Density and transition temperatures.
Melting Point (Solidus)
Liquidus Temperature
Same in both: Density 8.53 g/cm³0.31 lb/in³
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Min Service Temperature
Same in both: Max Service Temperature (continuous) 200°C392 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Polishability
Same in both: Machinability 30 / 100 · Machinability Rating (AISI 1212 = 100 %) 30%
Sustainability
Primary-production footprint per kilogram.
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Same in both: Embodied Energy (primary production) 55 MJ/kg23,646 BTU/lb
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Thermal Diffusivity
Thermal Shock Resistance Index
Same in both: Specific Stiffness (E / density) 12.9 MN·m/kg · Modulus of Resilience 50 kJ/m³
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | C26000 | C68300 |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Default condition | O | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | 0.8 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| Chrome Plating | Yes | — |
| Electropolishing | Yes | — |
| Nickel Plating | Yes | — |
| Painting | Yes | — |
| Tin Plating | Yes | — |
They share 4 finishes: Copper Plating, Electroless Nickel (EN), Gold Plating, Silver Plating.
C26000 vs C68300 — frequently asked
What is the difference between C26000 and C68300?
Copper Alloy C26000 and C68300 are both copper alloy grades. Both yield at about 105 MPa — strength does not separate them. C26000 is the more ductile: elongation 62% versus 55% for C68300, and C68300 is harder (58 HB vs 55 HB).
Which is cheaper, C26000 or C68300?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which welds better, C26000 or C68300?
C68300. Its weldability rates good (55/100) against fair (40/100) for C26000.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C26000 and C68300 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.