Copper Alloy C26000 vs C48500
Copper Alloy · grade comparison
Copper Alloy C26000 and C48500 are both copper alloy grades. C48500 is the stronger of the two: yield strength 280 MPa (40.6 ksi) against 105 MPa (15.2 ksi) for C26000, about 167% more; tensile strength follows at 470 MPa (68.2 ksi) vs 325 MPa (47.1 ksi). In exchange, C26000 is the more ductile: elongation 62% versus 25% for C48500, and C48500 is harder (125 HB vs 55 HB). C26000 is stiffer (110 GPa vs 100 GPa). On the shop floor, C48500 machines more easily (very good vs poor), C26000 welds better (fair vs poor), and C26000 sits in a lower cost tier (high, $$$$) than C48500 (specialty, $$$$$).
C26000Choose it when the part is bent, formed or impact-loaded, or when it will be welded.
C48500Choose it when strength drives the design, or when the part is machined in volume.
C26000 vs C48500: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Vickers
Hardness, Rockwell B
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Same in both: Max Service Temperature (continuous) 200°C392 °F · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.28 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Carbon (primary production)
Typical Recycled Content
Same in both: Embodied Energy (primary production) 55 MJ/kg23,646 BTU/lb · Embodied Water 250 L/kg30 gal/lb
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | C26000 | C48500 |
|---|---|---|
| Default condition | O | H02 |
| Relative cost | $$$$ High | $$$$$ Specialty |
| Min. machined wall | 0.8 mm | 0.8 mm |
| Best machined surface | Ra 1.6 µm | Ra 1.6 µm |
Both are offered for CNC machining and Sheet metal. Both take the same 9 finishes: Chrome Plating, Copper Plating, Electroless Nickel (EN), Electropolishing, Gold Plating, Nickel Plating, Painting, Silver Plating, Tin Plating.
C26000 vs C48500 — frequently asked
Is C48500 stronger than C26000?
Yes. C48500 has a typical yield strength of 280 MPa (40.6 ksi) against 105 MPa (15.2 ksi) for C26000 — about 167% more. Tensile strength is 470 MPa (68.2 ksi) vs 325 MPa (47.1 ksi).
Which is cheaper, C26000 or C48500?
C26000 is the lower-cost material: it sits in the high tier ($$$$) while C48500 is specialty ($$$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, C26000 or C48500?
C48500. Its machinability rates very good (80/100) against poor (30/100) for C26000; for welding the order is C26000 first (fair, 40/100) then C48500 (poor, 20/100).