Copper Alloy C24000-H02 vs C24000-H06
Copper Alloy · C24000 temper comparison
C24000-H02 and C24000-H06 are two conditions of the same copper alloy grade, C24000: H02 (half hard) versus H06 (extra hard). The chemistry is identical, so every difference below comes from the condition. C24000-H06 is the stronger of the two: yield strength 480 MPa (69.6 ksi) against 310 MPa (45 ksi) for C24000-H02, about 55% more; tensile strength follows at 570 MPa (82.7 ksi) vs 395 MPa (57.3 ksi). In exchange, C24000-H02 is the more ductile: elongation 30% versus 5% for C24000-H06, and C24000-H06 is harder (165 HB vs 120 HB). C24000-H02 runs hotter in service (175°C vs 150°C continuous).
C24000-H02Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
C24000-H06Choose it when strength drives the design.
C24000-H02 vs C24000-H06: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 105 GPa15.2 Msi · Shear Modulus 39 GPa5.7 Msi · Bulk Modulus 112 GPa16.2 Msi · Poisson's Ratio 0.34
Physical
Density and transition temperatures.
Same in both: Density 8.67 g/cm³0.31 lb/in³ · Melting Point (Solidus) 1,000°C1,832 °F · Liquidus Temperature 1,030°C1,886 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 138 W/m·K79.7 BTU/hr·ft·°F · Specific Heat Capacity 375 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 18.4 µm/m·K10.2 µin/in·°F · Latent Heat of Fusion 180 J/g77.4 BTU/lb · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 32 % IACS · Electrical Resistivity 5.4×10⁻⁸ Ω·m2.13 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.26 V · Corrosion Resistance 60 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Machinability 32 / 100 · Weldability 45 / 100 · Castability 30 / 100 · Brazeability / Solderability 90 / 100 · Polishability 85 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 58 MJ/kg24,936 BTU/lb · Embodied Carbon (primary production) 4 kg CO₂/kg · Embodied Water 400 L/kg47.9 gal/lb · Typical Recycled Content 40%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C24000-H02 vs C24000-H06 — frequently asked
Is C24000-H06 stronger than C24000-H02?
Yes. C24000-H06 has a typical yield strength of 480 MPa (69.6 ksi) against 310 MPa (45 ksi) for C24000-H02 — about 55% more. Tensile strength is 570 MPa (82.7 ksi) vs 395 MPa (57.3 ksi).
Which condition does FabDigit quote by default, H02 or H06?
OS050 is the default C24000 condition in the FabDigit quote flow (neither H02 nor H06). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose C24000-H02 over C24000-H06?
Pick C24000-H02 when the part is bent, formed or impact-loaded, or when the part sees heat. Pick C24000-H06 when strength drives the design.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C24000-H02 and C24000-H06 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.