Copper Alloy C22600-H02 vs C22600-H08
Copper Alloy · C22600 temper comparison
C22600-H02 and C22600-H08 are two conditions of the same copper alloy grade, C22600: H02 (half hard) versus H08 (spring hard). The chemistry is identical, so every difference below comes from the condition. C22600-H08 is the stronger of the two: yield strength 483 MPa (70.1 ksi) against 330 MPa (47.9 ksi) for C22600-H02, about 46% more; tensile strength follows at 552 MPa (80.1 ksi) vs 400 MPa (58 ksi). In exchange, C22600-H02 is the more ductile: elongation 12% versus 3% for C22600-H08, and C22600-H08 is harder (155 HB vs 105 HB). C22600-H02 runs hotter in service (200°C vs 150°C continuous).
C22600-H02Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
C22600-H08Choose it when strength drives the design.
C22600-H02 vs C22600-H08: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Same in both: Elastic (Young's) Modulus 117 GPa17 Msi · Shear Modulus 44 GPa6.4 Msi · Bulk Modulus 118 GPa17.1 Msi · Poisson's Ratio 0.33
Physical
Density and transition temperatures.
Same in both: Density 8.8 g/cm³0.32 lb/in³ · Melting Point (Solidus) 1,005°C1,841 °F · Liquidus Temperature 1,030°C1,886 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 172 W/m·K99.4 BTU/hr·ft·°F · Specific Heat Capacity 376 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 18.5 µm/m·K10.3 µin/in·°F · Latent Heat of Fusion 205 J/g88.1 BTU/lb · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Same in both: Electrical Resistivity 4.3×10⁻⁸ Ω·m1.69 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.23 V · Corrosion Resistance 62 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Formability (cold)
Same in both: Machinability Rating (AISI 1212 = 100 %) 30% · Weldability 55 / 100 · Castability 35 / 100 · Brazeability / Solderability 92 / 100 · Polishability 90 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 58 MJ/kg24,936 BTU/lb · Embodied Carbon (primary production) 3.8 kg CO₂/kg · Embodied Water 290 L/kg34.7 gal/lb · Typical Recycled Content 50%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C22600-H02 vs C22600-H08 — frequently asked
Is C22600-H08 stronger than C22600-H02?
Yes. C22600-H08 has a typical yield strength of 483 MPa (70.1 ksi) against 330 MPa (47.9 ksi) for C22600-H02 — about 46% more. Tensile strength is 552 MPa (80.1 ksi) vs 400 MPa (58 ksi).
Which condition does FabDigit quote by default, H02 or H08?
H02 is the default C22600 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose C22600-H02 over C22600-H08?
Pick C22600-H02 when the part is bent, formed or impact-loaded, or when the part sees heat. Pick C22600-H08 when strength drives the design.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C22600-H02 and C22600-H08 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.