Copper Alloy C17410-TM00 vs C17410-TM06
Copper Alloy · C17410 temper comparison
C17410-TM00 and C17410-TM06 are two conditions of the same copper alloy grade, C17410: TM00 (mill hardened) versus TM06 (mill hardened, extra hard). The chemistry is identical, so every difference below comes from the condition. C17410-TM06 is the stronger of the two: yield strength 760 MPa (110 ksi) against 520 MPa (75.4 ksi) for C17410-TM00, about 46% more; tensile strength follows at 795 MPa (115 ksi) vs 620 MPa (89.9 ksi). In exchange, C17410-TM00 is the more ductile: elongation 16% versus 8% for C17410-TM06, and C17410-TM06 is harder (228 HV vs 180 HV). C17410-TM00 conducts heat better (225 W/m·K vs 200 W/m·K).
C17410-TM00Choose it when the part is bent, formed or impact-loaded.
C17410-TM06Choose it when strength drives the design.
C17410-TM00 vs C17410-TM06: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Rockwell B
Hardness, Vickers
Same in both: Shear Modulus 53 GPa7.7 Msi · Bulk Modulus 115 GPa16.7 Msi · Poisson's Ratio 0.3
Physical
Density and transition temperatures.
Same in both: Density 8.83 g/cm³0.32 lb/in³ · Melting Point (Solidus) 1,030°C1,886 °F · Liquidus Temperature 1,070°C1,958 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Same in both: Specific Heat Capacity 420 J/kg·K0.1 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 17.6 µm/m·K9.8 µin/in·°F · Latent Heat of Fusion 205 J/g88.1 BTU/lb · Max Service Temperature (continuous) 200°C392 °F · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.2 V · Corrosion Resistance 62 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Weldability
Formability (cold)
Same in both: Machinability 45 / 100 · Machinability Rating (AISI 1212 = 100 %) 35% · Castability 45 / 100 · Brazeability / Solderability 80 / 100 · Polishability 80 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 72 MJ/kg30,954 BTU/lb · Embodied Carbon (primary production) 5 kg CO₂/kg · Embodied Water 300 L/kg35.9 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C17410-TM00 vs C17410-TM06 — frequently asked
Is C17410-TM06 stronger than C17410-TM00?
Yes. C17410-TM06 has a typical yield strength of 760 MPa (110 ksi) against 520 MPa (75.4 ksi) for C17410-TM00 — about 46% more. Tensile strength is 795 MPa (115 ksi) vs 620 MPa (89.9 ksi).
Which condition does FabDigit quote by default, TM00 or TM06?
TM04 is the default C17410 condition in the FabDigit quote flow (neither TM00 nor TM06). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose C17410-TM00 over C17410-TM06?
Pick C17410-TM00 when the part is bent, formed or impact-loaded. Pick C17410-TM06 when strength drives the design.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C17410-TM00 and C17410-TM06 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.