Copper Alloy C11000 vs C81300
Copper Alloy · grade comparison
Copper Alloy C11000 and C81300 are both copper alloy grades. C81300 is the stronger of the two: yield strength 172 MPa (24.9 ksi) against 69 MPa (10 ksi) for C11000, about 149% more; tensile strength follows at 310 MPa (45 ksi) vs 221 MPa (32.1 ksi). In exchange, C11000 is the more ductile: elongation 45% versus 11% for C81300, and C81300 is harder (95 HB vs 45 HB). C81300 is stiffer (128 GPa vs 117 GPa) and C81300 runs hotter in service (350°C vs 250°C continuous). On the shop floor, C81300 machines more easily (fair vs poor) and C81300 welds better (good vs fair).
C11000Choose it when the part is bent, formed or impact-loaded.
C81300Choose it when strength drives the design, or when the part sees heat.
C11000 vs C81300: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Vickers
Hardness, Rockwell B
Physical
Density and transition temperatures.
Density
Liquidus Temperature
Same in both: Melting Point (Solidus) 1,065°C1,949 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Same in both: Latent Heat of Fusion 205 J/g88.1 BTU/lb · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Polishability
Same in both: Machinability Rating (AISI 1212 = 100 %) 20%
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Water
Typical Recycled Content
Same in both: Embodied Carbon (primary production) 3.6 kg CO₂/kg
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | C11000 | C81300 |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| 3D printing | Yes | — |
| Default condition | O | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | 0.8 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| Chrome Plating | Yes | — |
| Electropolishing | Yes | — |
| Nickel Plating | Yes | — |
| Painting | Yes | — |
| Tin Plating | Yes | — |
They share 4 finishes: Copper Plating, Electroless Nickel (EN), Gold Plating, Silver Plating.
C11000 vs C81300 — frequently asked
Is C81300 stronger than C11000?
Yes. C81300 has a typical yield strength of 172 MPa (24.9 ksi) against 69 MPa (10 ksi) for C11000 — about 149% more. Tensile strength is 310 MPa (45 ksi) vs 221 MPa (32.1 ksi).
Which is cheaper, C11000 or C81300?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, C11000 or C81300?
C81300. Its machinability rates fair (35/100) against poor (25/100) for C11000; for welding the order is C81300 first (good, 60/100) then C11000 (fair, 35/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in C11000 and C81300 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.