Copper Alloy C1100-F vs C1100-H
Copper Alloy · C1100 temper comparison
C1100-F and C1100-H are two conditions of the same copper alloy grade, C1100: F (as fabricated) versus H (hardened). The chemistry is identical, so every difference below comes from the condition. C1100-H is the stronger of the two: yield strength 305 MPa (44.2 ksi) against 75 MPa (10.9 ksi) for C1100-F, about 4.1 times as much; tensile strength follows at 345 MPa (50 ksi) vs 215 MPa (31.2 ksi). In exchange, C1100-F is the more ductile: elongation 42% versus 6% for C1100-H, and C1100-H is harder (112 HV vs 50 HV). C1100-F runs hotter in service (200°C vs 150°C continuous). On the shop floor, C1100-H machines more easily (32 vs 20 out of 100).
C1100-FChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
C1100-HChoose it when strength drives the design, or when the part is machined in volume.
C1100-F vs C1100-H: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 117 GPa17 Msi · Shear Modulus 44 GPa6.4 Msi · Bulk Modulus 140 GPa20.3 Msi · Poisson's Ratio 0.34 · Hardness, Brinell 45 HB
Physical
Density and transition temperatures.
Same in both: Density 8.94 g/cm³0.32 lb/in³ · Melting Point (Solidus) 1,065°C1,949 °F · Liquidus Temperature 1,083°C1,981 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 385 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 17.7 µm/m·K9.8 µin/in·°F · Latent Heat of Fusion 205 J/g88.1 BTU/lb · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.3 V · Corrosion Resistance 62 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Formability (cold)
Same in both: Machinability Rating (AISI 1212 = 100 %) 20% · Weldability 45 / 100 · Brazeability / Solderability 92 / 100 · Polishability 80 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 55 MJ/kg23,646 BTU/lb · Embodied Carbon (primary production) 3.8 kg CO₂/kg · Embodied Water 320 L/kg38.3 gal/lb · Typical Recycled Content 35%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C1100-F vs C1100-H — frequently asked
Is C1100-H stronger than C1100-F?
Yes. C1100-H has a typical yield strength of 305 MPa (44.2 ksi) against 75 MPa (10.9 ksi) for C1100-F — about 4.1 times as much. Tensile strength is 345 MPa (50 ksi) vs 215 MPa (31.2 ksi).
Which condition does FabDigit quote by default, F or H?
O is the default C1100 condition in the FabDigit quote flow (neither F nor H). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, C1100-F or C1100-H?
C1100-H, by a small margin. Both rate poor for machinability — 32/100 against 20/100 for C1100-F.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C1100-F and C1100-H side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.