Copper Alloy C10300-H02 vs C10300-H04
Copper Alloy · C10300 temper comparison
C10300-H02 and C10300-H04 are two conditions of the same copper alloy grade, C10300: H02 (half hard) versus H04 (full hard). The chemistry is identical, so every difference below comes from the condition. C10300-H04 is the stronger of the two: yield strength 280 MPa (40.6 ksi) against 245 MPa (35.5 ksi) for C10300-H02, about 14% more; tensile strength follows at 315 MPa (45.7 ksi) vs 280 MPa (40.6 ksi). In exchange, C10300-H02 is the more ductile: elongation 14% versus 6% for C10300-H04, and C10300-H04 is harder (92 HB vs 78 HB).
C10300-H02Choose it when the part is bent, formed or impact-loaded.
C10300-H04Choose it when strength drives the design.
C10300-H02 vs C10300-H04: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 117 GPa17 Msi · Shear Modulus 44 GPa6.4 Msi · Bulk Modulus 140 GPa20.3 Msi · Poisson's Ratio 0.34 · Charpy V-Notch Impact (RT) 70 J51.6 ft·lbf
Physical
Density and transition temperatures.
Same in both: Density 8.94 g/cm³0.32 lb/in³ · Melting Point (Solidus) 1,083°C1,981 °F · Liquidus Temperature 1,083°C1,981 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 385 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 17.6 µm/m·K9.8 µin/in·°F · Latent Heat of Fusion 205 J/g88.1 BTU/lb · Min Service Temperature -269°C-452 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.25 V · Corrosion Resistance 65 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Machinability 22 / 100 · Castability 45 / 100 · Brazeability / Solderability 95 / 100 · Polishability 80 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 57 MJ/kg24,506 BTU/lb · Embodied Carbon (primary production) 3.6 kg CO₂/kg · Embodied Water 250 L/kg30 gal/lb · Typical Recycled Content 25%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C10300-H02 vs C10300-H04 — frequently asked
Is C10300-H04 stronger than C10300-H02?
Yes. C10300-H04 has a typical yield strength of 280 MPa (40.6 ksi) against 245 MPa (35.5 ksi) for C10300-H02 — about 14% more. Tensile strength is 315 MPa (45.7 ksi) vs 280 MPa (40.6 ksi).
Which condition does FabDigit quote by default, H02 or H04?
O60 is the default C10300 condition in the FabDigit quote flow (neither H02 nor H04). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which welds better, C10300-H02 or C10300-H04?
C10300-H02. Its weldability rates very good (80/100) against very good (75/100) for C10300-H04.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C10300-H02 and C10300-H04 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.