G-9 vs XXP
Composite · grade comparison
G-9 and XXP are both composite grades. G-9 is the stronger of the two: tensile strength 240 MPa (34.8 ksi) against 83 MPa (12 ksi) for XXP, about 189% more. XXP is lighter (1.35 g/cm³ vs 1.95 g/cm³ for G-9) and G-9 is stiffer (19 GPa vs 8 GPa). On the shop floor, XXP machines more easily (very good vs poor) and XXP sits in a lower cost tier (standard, $$) than G-9 (high, $$$$).
G-9Choose it when strength drives the design, or when the part sees heat.
XXPChoose it when weight is the constraint, or when the part is machined in volume.
G-9 vs XXP: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all composite grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all composite grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Compressive Strength
Compressive Modulus
Flexural Strength
Flexural Modulus
Shear Strength
Izod Impact, Notched
Hardness, Rockwell M
Physical
Density and transition temperatures.
Density
Water Absorption (Saturation)
Glass Transition (Tg)
Same in both: Water Absorption (24 h) 0.8%
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Limiting Oxygen Index
Max Service Temperature (short-term)
Electrical
Conductivity and insulation.
Electrical Resistivity
Dielectric Strength
Dielectric Constant (1 MHz)
Dissipation Factor (1 MHz)
Volume Resistivity
Surface Resistivity
Comparative Tracking Index (CTI)
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
UV / Weathering Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Same in both: Embodied Water 200 L/kg24 gal/lb · Typical Recycled Content 0%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Same in both: Thermal Diffusivity 0.1 mm²/s · Thermal Shock Resistance Index 0
Strength versus weight
Yield strength against density for every composite grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | G-9 | XXP |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$ Standard |
| Min. machined wall | — | — |
| Best machined surface | — | — |
G-9 vs XXP — frequently asked
Is G-9 stronger than XXP?
Yes. G-9 has a typical tensile strength of 240 MPa (34.8 ksi) against 83 MPa (12 ksi) for XXP — about 189% more.
Which is cheaper, G-9 or XXP?
XXP is the lower-cost material: it sits in the standard tier ($$) while G-9 is high ($$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, G-9 or XXP?
XXP. Its machinability rates very good (75/100) against poor (30/100) for G-9.
Ready to make it?
Upload a CAD file and FabDigit prices the part in G-9 and XXP side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.