Cobalt-Chrome Alloy F1537 Alloy 1 vs Stellite 6
Cobalt-Chrome Alloy · grade comparison
Cobalt-Chrome Alloy F1537 Alloy 1 and Stellite 6 are both cobalt-chrome alloy grades. F1537 Alloy 1 is the stronger of the two: yield strength 610 MPa (88.5 ksi) against 541 MPa (78.5 ksi) for Stellite 6, about 13% more; tensile strength follows at 1,000 MPa (145 ksi) vs 834 MPa (121 ksi). F1537 Alloy 1 is the more ductile: elongation 35% versus 1% for Stellite 6, and Stellite 6 is harder (40 HRC vs 29 HRC). Stellite 6 runs hotter in service (800°C vs 600°C continuous). On the shop floor, F1537 Alloy 1 sits in a lower cost tier (high, $$$$) than Stellite 6 (specialty, $$$$$).
F1537 Alloy 1Choose it when strength drives the design, or when the part is bent, formed or impact-loaded.
Stellite 6Choose it when the part sees heat.
F1537 Alloy 1 vs Stellite 6: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all cobalt-chrome alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all cobalt-chrome alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Same in both: Poisson's Ratio 0.3
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Same in both: Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Resistivity
Same in both: Electrical Conductivity 1.9 % IACS
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.25 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Castability
Brazeability / Solderability
Polishability
Same in both: Weldability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every cobalt-chrome alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | F1537 Alloy 1 | Stellite 6 |
|---|---|---|
| Default condition | — | As Cast |
| Relative cost | $$$$ High | $$$$$ Specialty |
| Min. machined wall | — | — |
| Best machined surface | — | — |
F1537 Alloy 1 vs Stellite 6 — frequently asked
Is F1537 Alloy 1 stronger than Stellite 6?
Yes. F1537 Alloy 1 has a typical yield strength of 610 MPa (88.5 ksi) against 541 MPa (78.5 ksi) for Stellite 6 — about 13% more. Tensile strength is 1,000 MPa (145 ksi) vs 834 MPa (121 ksi).
Which is cheaper, F1537 Alloy 1 or Stellite 6?
F1537 Alloy 1 is the lower-cost material: it sits in the high tier ($$$$) while Stellite 6 is specialty ($$$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, F1537 Alloy 1 or Stellite 6?
F1537 Alloy 1, by a small margin. Both rate not recommended for machinability — 14/100 against 8/100 for Stellite 6.
Ready to make it?
Upload a CAD file and FabDigit prices the part in F1537 Alloy 1 and Stellite 6 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.