MG Carbon Brush vs UHP Graphite Electrode
Ceramic · grade comparison
MG Carbon Brush and UHP Graphite Electrode are both ceramic grades. MG Carbon Brush is the stronger of the two: tensile strength 20 MPa (2.9 ksi) against 8 MPa (1.16 ksi) for UHP Graphite Electrode, about 150% more. UHP Graphite Electrode is lighter (1.7 g/cm³ vs 3.6 g/cm³ for MG Carbon Brush) and MG Carbon Brush is stiffer (13 GPa vs 12 GPa). On the shop floor, UHP Graphite Electrode sits in a lower cost tier (standard, $$) than MG Carbon Brush (high, $$$$).
MG Carbon BrushChoose it when strength drives the design.
UHP Graphite ElectrodeChoose it when weight is the constraint, or when the part sees heat.
MG Carbon Brush vs UHP Graphite Electrode: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all ceramic grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all ceramic grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
MG Carbon BrushUHP Graphite Electrode
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Compressive Strength
Flexural Strength
Shear Strength
Hardness, Vickers
Hardness, Mohs
Elongation at Break
Fracture Toughness (K_IC)
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Porosity
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Electrical
Conductivity and insulation.
Electrical Resistivity
Volume Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Polishability
Sintering / Firing Temperature
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every ceramic grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | MG Carbon Brush | UHP Graphite Electrode |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$ Standard |
| Min. machined wall | — | — |
| Best machined surface | — | — |
MG Carbon Brush vs UHP Graphite Electrode — frequently asked
Is MG Carbon Brush stronger than UHP Graphite Electrode?
Yes. MG Carbon Brush has a typical tensile strength of 20 MPa (2.9 ksi) against 8 MPa (1.16 ksi) for UHP Graphite Electrode — about 150% more.
Which is cheaper, MG Carbon Brush or UHP Graphite Electrode?
UHP Graphite Electrode is the lower-cost material: it sits in the standard tier ($$) while MG Carbon Brush is high ($$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, MG Carbon Brush or UHP Graphite Electrode?
UHP Graphite Electrode, by a small margin. Both rate excellent for machinability — 90/100 against 85/100 for MG Carbon Brush.
Ready to make it?
Upload a CAD file and FabDigit prices the part in MG Carbon Brush and UHP Graphite Electrode side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.