Glassy Carbon vs Isostatic Graphite
Ceramic · grade comparison
Glassy Carbon and Isostatic Graphite are both ceramic grades. Glassy Carbon is the stronger of the two: tensile strength 130 MPa (18.9 ksi) against 27 MPa (3.92 ksi) for Isostatic Graphite, about 4.8 times as much. Glassy Carbon is lighter (1.42 g/cm³ vs 1.77 g/cm³ for Isostatic Graphite) and Glassy Carbon is stiffer (35 GPa vs 11 GPa). On the shop floor, Isostatic Graphite machines more easily (excellent vs not recommended).
Glassy CarbonChoose it when strength drives the design, or when weight is the constraint.
Isostatic GraphiteChoose it when the part is machined in volume.
Glassy Carbon vs Isostatic Graphite: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all ceramic grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all ceramic grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Glassy CarbonIsostatic Graphite
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Elongation at Break
Compressive Strength
Flexural Strength
Shear Strength
Fracture Toughness (K_IC)
Hardness, Vickers
Hardness, Knoop
Hardness, Mohs
Physical
Density and transition temperatures.
Density
Porosity
Melting Point (Solidus)
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 710 J/kg·K0.17 BTU/lb·°F · Min Service Temperature -269°C-452 °F
Electrical
Conductivity and insulation.
Electrical Resistivity
Volume Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Polishability
Sintering / Firing Temperature
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every ceramic grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | Glassy Carbon | Isostatic Graphite |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Glassy Carbon vs Isostatic Graphite — frequently asked
Is Glassy Carbon stronger than Isostatic Graphite?
Yes. Glassy Carbon has a typical tensile strength of 130 MPa (18.9 ksi) against 27 MPa (3.92 ksi) for Isostatic Graphite — about 4.8 times as much.
Which is cheaper, Glassy Carbon or Isostatic Graphite?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, Glassy Carbon or Isostatic Graphite?
Isostatic Graphite. Its machinability rates excellent (90/100) against not recommended (12/100) for Glassy Carbon.
Ready to make it?
Upload a CAD file and FabDigit prices the part in Glassy Carbon and Isostatic Graphite side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.