Extruded Graphite vs Glassy Carbon
Ceramic · grade comparison
Extruded Graphite and Glassy Carbon are both ceramic grades. Glassy Carbon is the stronger of the two: tensile strength 130 MPa (18.9 ksi) against 9 MPa (1.31 ksi) for Extruded Graphite, about 14 times as much. Glassy Carbon is the more ductile: elongation 0.4% versus 0.25% for Extruded Graphite. Glassy Carbon is lighter (1.42 g/cm³ vs 1.7 g/cm³ for Extruded Graphite) and Glassy Carbon is stiffer (35 GPa vs 10 GPa). On the shop floor, Extruded Graphite machines more easily (excellent vs not recommended) and Extruded Graphite sits in a lower cost tier (premium, $$$) than Glassy Carbon (high, $$$$).
Extruded GraphiteChoose it when the part sees heat, or when the part is machined in volume.
Glassy CarbonChoose it when strength drives the design, or when the part is bent, formed or impact-loaded.
Extruded Graphite vs Glassy Carbon: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all ceramic grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all ceramic grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Extruded GraphiteGlassy Carbon
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Elongation at Break
Compressive Strength
Flexural Strength
Shear Strength
Fracture Toughness (K_IC)
Hardness, Mohs
Bulk Modulus
Hardness, Vickers
Hardness, Knoop
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Porosity
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Specific Heat Capacity 710 J/kg·K0.17 BTU/lb·°F
Electrical
Conductivity and insulation.
Electrical Resistivity
Volume Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Polishability
Sintering / Firing Temperature
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every ceramic grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | Extruded Graphite | Glassy Carbon |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$ Premium | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Extruded Graphite vs Glassy Carbon — frequently asked
Is Glassy Carbon stronger than Extruded Graphite?
Yes. Glassy Carbon has a typical tensile strength of 130 MPa (18.9 ksi) against 9 MPa (1.31 ksi) for Extruded Graphite — about 14 times as much.
Which is cheaper, Extruded Graphite or Glassy Carbon?
Extruded Graphite is the lower-cost material: it sits in the premium tier ($$$) while Glassy Carbon is high ($$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, Extruded Graphite or Glassy Carbon?
Extruded Graphite. Its machinability rates excellent (88/100) against not recommended (12/100) for Glassy Carbon.
Ready to make it?
Upload a CAD file and FabDigit prices the part in Extruded Graphite and Glassy Carbon side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.