Aluminum ZL104-T1 vs ZL104-T6
Aluminum · ZL104 temper comparison
ZL104-T1 and ZL104-T6 are two conditions of the same aluminum grade, ZL104: T1 (cooled from hot working and naturally aged) versus T6 (solution heat treated and artificially aged). The chemistry is identical, so every difference below comes from the condition. ZL104-T6 is the stronger of the two: yield strength 200 MPa (29 ksi) against 150 MPa (21.8 ksi) for ZL104-T1, about 33% more; tensile strength follows at 260 MPa (37.7 ksi) vs 220 MPa (31.9 ksi). ZL104-T6 is the more ductile: elongation 3% versus 2% for ZL104-T1, and ZL104-T6 is harder (75 HB vs 68 HB).
ZL104-T6Choose it when strength drives the design, or when the part is bent, formed or impact-loaded.
ZL104-T1 vs ZL104-T6: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Same in both: Elastic (Young's) Modulus 71 GPa10.3 Msi · Shear Modulus 26.5 GPa3.8 Msi · Bulk Modulus 70 GPa10.2 Msi · Poisson's Ratio 0.33 · Fracture Toughness (K_IC) 19 MPa·√m17.3 ksi·√in · Charpy V-Notch Impact (RT) 6 J4.4 ft·lbf
Physical
Density and transition temperatures.
Same in both: Density 2.65 g/cm³0.1 lb/in³ · Melting Point (Solidus) 557°C1,035 °F · Liquidus Temperature 596°C1,105 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 963 J/kg·K0.23 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 21.5 µm/m·K11.9 µin/in·°F · Latent Heat of Fusion 400 J/g172 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Same in both: Electrical Resistivity 5.2×10⁻⁸ Ω·m2.05 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.83 V · Corrosion Resistance 58 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Same in both: Machinability Rating (AISI 1212 = 100 %) 90% · Weldability 70 / 100 · Formability (cold) 10 / 100 · Castability 90 / 100 · Brazeability / Solderability 25 / 100 · Polishability 45 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 200 MJ/kg85,985 BTU/lb · Embodied Carbon (primary production) 12.5 kg CO₂/kg · Embodied Water 1,200 L/kg144 gal/lb · Typical Recycled Content 70%
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
ZL104-T1 vs ZL104-T6 — frequently asked
Is ZL104-T6 stronger than ZL104-T1?
Yes. ZL104-T6 has a typical yield strength of 200 MPa (29 ksi) against 150 MPa (21.8 ksi) for ZL104-T1 — about 33% more. Tensile strength is 260 MPa (37.7 ksi) vs 220 MPa (31.9 ksi).
Which condition does FabDigit quote by default, T1 or T6?
T6 is the default ZL104 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose ZL104-T1 over ZL104-T6?
Pick ZL104-T6 when strength drives the design, or when the part is bent, formed or impact-loaded.
Ready to make it?
Upload a CAD file and FabDigit prices the part in ZL104-T1 and ZL104-T6 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.