Aluminum AlSi12 vs EN AC-43100
Aluminum · grade comparison
Aluminum AlSi12 and EN AC-43100 are both aluminum grades. AlSi12 is the stronger of the two: yield strength 250 MPa (36.3 ksi) against 110 MPa (16 ksi) for EN AC-43100, about 127% more; tensile strength follows at 400 MPa (58 ksi) vs 200 MPa (29 ksi). AlSi12 is the more ductile: elongation 5% versus 2.5% for EN AC-43100, and AlSi12 is harder (105 HB vs 60 HB). EN AC-43100 runs hotter in service (150°C vs 120°C continuous) and EN AC-43100 conducts heat better (150 W/m·K vs 120 W/m·K). On the shop floor, AlSi12 welds better (very good vs good) and EN AC-43100 sits in a lower cost tier (standard, $$) than AlSi12 (premium, $$$).
AlSi12Choose it when strength drives the design, or when the part is bent, formed or impact-loaded.
EN AC-43100Choose it when the part sees heat, or when cost is the deciding factor.
AlSi12 vs EN AC-43100: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Vickers
Same in both: Poisson's Ratio 0.33 · Fracture Toughness (K_IC) 17 MPa·√m15.5 ksi·√in
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Same in both: Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.83 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Formability (cold)
Brazeability / Solderability
Polishability
Machinability Rating (AISI 1212 = 100 %)
Same in both: Castability 95 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | AlSi12 | EN AC-43100 |
|---|---|---|
| 3D printing | Yes | — |
| Default condition | As Printed | — |
| Relative cost | $$$ Premium | $$ Standard |
| Min. machined wall | — | — |
| Best machined surface | — | — |
| Anodized (Aluminum AM) | Yes | — |
| Plated (Metal AM) | Yes | — |
They share 4 finishes: Electroless Nickel (EN), Epoxy Coating, Gold Plating, Silver Plating.
AlSi12 vs EN AC-43100 — frequently asked
Is AlSi12 stronger than EN AC-43100?
Yes. AlSi12 has a typical yield strength of 250 MPa (36.3 ksi) against 110 MPa (16 ksi) for EN AC-43100 — about 127% more. Tensile strength is 400 MPa (58 ksi) vs 200 MPa (29 ksi).
Which is cheaper, AlSi12 or EN AC-43100?
EN AC-43100 is the lower-cost material: it sits in the standard tier ($$) while AlSi12 is premium ($$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which welds better, AlSi12 or EN AC-43100?
AlSi12. Its weldability rates very good (80/100) against good (65/100) for EN AC-43100.
Ready to make it?
Upload a CAD file and FabDigit prices the part in AlSi12 and EN AC-43100 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.