Aluminum AlMgSc-SR vs AlMgSc-T5
Aluminum · AlMgSc temper comparison
AlMgSc-SR and AlMgSc-T5 are two conditions of the same aluminum grade, AlMgSc: SR (stress relieved) versus T5 (cooled from hot working and artificially aged). The chemistry is identical, so every difference below comes from the condition. AlMgSc-T5 is the stronger of the two: yield strength 460 MPa (66.7 ksi) against 400 MPa (58 ksi) for AlMgSc-SR, about 15% more; tensile strength follows at 500 MPa (72.5 ksi) vs 470 MPa (68.2 ksi). In exchange, AlMgSc-SR is the more ductile: elongation 14% versus 12% for AlMgSc-T5, and AlMgSc-T5 is harder (140 HB vs 126 HB).
AlMgSc-SRChoose it when the part is bent, formed or impact-loaded.
AlMgSc-T5Choose it when strength drives the design.
AlMgSc-SR vs AlMgSc-T5: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 70 GPa10.2 Msi · Shear Modulus 26.5 GPa3.8 Msi · Bulk Modulus 69 GPa10 Msi · Poisson's Ratio 0.33 · Compressive Strength 470 MPa68.2 ksi · Shear Strength 295 MPa42.8 ksi · Fracture Toughness (K_IC) 33 MPa·√m30 ksi·√in · Hardness, Rockwell B 80 HRB
Physical
Density and transition temperatures.
Same in both: Density 2.67 g/cm³0.1 lb/in³ · Melting Point (Solidus) 585°C1,085 °F · Liquidus Temperature 645°C1,193 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Same in both: Specific Heat Capacity 900 J/kg·K0.21 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 23.5 µm/m·K13.1 µin/in·°F · Latent Heat of Fusion 390 J/g168 BTU/lb · Max Service Temperature (continuous) 150°C302 °F · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Same in both: Electrical Resistivity 6.2×10⁻⁸ Ω·m2.44 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.87 V · Corrosion Resistance 68 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Same in both: Machinability Rating (AISI 1212 = 100 %) 110% · Weldability 85 / 100 · Formability (cold) 45 / 100 · Castability 50 / 100 · Brazeability / Solderability 30 / 100 · Polishability 60 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 260 MJ/kg111,780 BTU/lb · Embodied Carbon (primary production) 24 kg CO₂/kg · Embodied Water 1,200 L/kg144 gal/lb · Typical Recycled Content 5%
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
AlMgSc-SR vs AlMgSc-T5 — frequently asked
Is AlMgSc-T5 stronger than AlMgSc-SR?
Yes. AlMgSc-T5 has a typical yield strength of 460 MPa (66.7 ksi) against 400 MPa (58 ksi) for AlMgSc-SR — about 15% more. Tensile strength is 500 MPa (72.5 ksi) vs 470 MPa (68.2 ksi).
Which condition does FabDigit quote by default, SR or T5?
T5 is the default AlMgSc condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose AlMgSc-SR over AlMgSc-T5?
Pick AlMgSc-SR when the part is bent, formed or impact-loaded. Pick AlMgSc-T5 when strength drives the design.
Ready to make it?
Upload a CAD file and FabDigit prices the part in AlMgSc-SR and AlMgSc-T5 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.