Aluminum AlMgSc-O vs AlMgSc-T5
Aluminum · AlMgSc temper comparison
AlMgSc-O and AlMgSc-T5 are two conditions of the same aluminum grade, AlMgSc: O (annealed) versus T5 (cooled from hot working and artificially aged). The chemistry is identical, so every difference below comes from the condition. AlMgSc-T5 is the stronger of the two: yield strength 460 MPa (66.7 ksi) against 200 MPa (29 ksi) for AlMgSc-O, about 130% more; tensile strength follows at 500 MPa (72.5 ksi) vs 330 MPa (47.9 ksi). In exchange, AlMgSc-O is the more ductile: elongation 21% versus 12% for AlMgSc-T5, and AlMgSc-T5 is harder (140 HB vs 80 HB). AlMgSc-O runs hotter in service (200°C vs 150°C continuous) and AlMgSc-O conducts heat better (130 W/m·K vs 110 W/m·K).
AlMgSc-OChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
AlMgSc-T5Choose it when strength drives the design.
AlMgSc-O vs AlMgSc-T5: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Shear Modulus 26.5 GPa3.8 Msi · Bulk Modulus 69 GPa10 Msi · Poisson's Ratio 0.33
Physical
Density and transition temperatures.
Same in both: Density 2.67 g/cm³0.1 lb/in³ · Melting Point (Solidus) 585°C1,085 °F · Liquidus Temperature 645°C1,193 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 900 J/kg·K0.21 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 23.5 µm/m·K13.1 µin/in·°F · Latent Heat of Fusion 390 J/g168 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.87 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 50 / 100 · Brazeability / Solderability 30 / 100 · Polishability 60 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 260 MJ/kg111,780 BTU/lb · Embodied Carbon (primary production) 24 kg CO₂/kg · Embodied Water 1,200 L/kg144 gal/lb · Typical Recycled Content 5%
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
AlMgSc-O vs AlMgSc-T5 — frequently asked
Is AlMgSc-T5 stronger than AlMgSc-O?
Yes. AlMgSc-T5 has a typical yield strength of 460 MPa (66.7 ksi) against 200 MPa (29 ksi) for AlMgSc-O — about 130% more. Tensile strength is 500 MPa (72.5 ksi) vs 330 MPa (47.9 ksi).
Which condition does FabDigit quote by default, O or T5?
T5 is the default AlMgSc condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, AlMgSc-O or AlMgSc-T5?
AlMgSc-T5. Its machinability rates good (55/100) against fair (50/100) for AlMgSc-O.