Aluminum AC8C-T5 vs AC8C-T7
Aluminum · AC8C temper comparison
AC8C-T5 and AC8C-T7 are two conditions of the same aluminum grade, AC8C: T5 (cooled from hot working and artificially aged) versus T7 (solution heat treated and overaged (stabilized)). The chemistry is identical, so every difference below comes from the condition. AC8C-T7 is the stronger of the two: yield strength 200 MPa (29 ksi) against 175 MPa (25.4 ksi) for AC8C-T5, about 14% more; tensile strength follows at 235 MPa (34.1 ksi) vs 215 MPa (31.2 ksi). AC8C-T7 is the more ductile: elongation 1.3% versus 1% for AC8C-T5, and AC8C-T7 is harder (100 HB vs 95 HB). AC8C-T7 runs hotter in service (250°C vs 210°C continuous).
AC8C-T7Choose it when strength drives the design, or when the part is bent, formed or impact-loaded.
AC8C-T5 vs AC8C-T7: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Same in both: Elastic (Young's) Modulus 80 GPa11.6 Msi · Shear Modulus 30 GPa4.4 Msi · Bulk Modulus 76 GPa11 Msi · Poisson's Ratio 0.33 · Compressive Strength 265 MPa38.4 ksi · Fracture Toughness (K_IC) 16 MPa·√m14.6 ksi·√in · Charpy V-Notch Impact (RT) 2 J1.5 ft·lbf
Physical
Density and transition temperatures.
Same in both: Density 2.74 g/cm³0.1 lb/in³ · Melting Point (Solidus) 520°C968 °F · Liquidus Temperature 590°C1,094 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 900 J/kg·K0.21 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 20.5 µm/m·K11.4 µin/in·°F · Latent Heat of Fusion 389 J/g167 BTU/lb · Min Service Temperature -60°C-76 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Same in both: Electrical Resistivity 7.2×10⁻⁸ Ω·m2.83 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.8 V · Corrosion Resistance 42 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Same in both: Machinability Rating (AISI 1212 = 100 %) 60% · Weldability 30 / 100 · Formability (cold) 5 / 100 · Castability 82 / 100 · Brazeability / Solderability 20 / 100 · Polishability 45 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 200 MJ/kg85,985 BTU/lb · Embodied Carbon (primary production) 12.5 kg CO₂/kg · Embodied Water 1,100 L/kg132 gal/lb · Typical Recycled Content 55%
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
AC8C-T5 vs AC8C-T7 — frequently asked
Is AC8C-T7 stronger than AC8C-T5?
Yes. AC8C-T7 has a typical yield strength of 200 MPa (29 ksi) against 175 MPa (25.4 ksi) for AC8C-T5 — about 14% more. Tensile strength is 235 MPa (34.1 ksi) vs 215 MPa (31.2 ksi).
Which condition does FabDigit quote by default, T5 or T7?
T6 is the default AC8C condition in the FabDigit quote flow (neither T5 nor T7). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose AC8C-T5 over AC8C-T7?
Pick AC8C-T7 when strength drives the design, or when the part is bent, formed or impact-loaded.
Ready to make it?
Upload a CAD file and FabDigit prices the part in AC8C-T5 and AC8C-T7 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.