Aluminum 8011 vs 8017
Aluminum · grade comparison
Aluminum 8011 and 8017 are both aluminum grades. 8011 is the stronger of the two: yield strength 120 MPa (17.4 ksi) against 95 MPa (13.8 ksi) for 8017, about 26% more; tensile strength follows at 145 MPa (21 ksi) vs 115 MPa (16.7 ksi). In exchange, 8017 is the more ductile: elongation 14% versus 4% for 8011, and 8011 is harder (42 HB vs 32 HB). 8011 runs hotter in service (150°C vs 125°C continuous) and 8017 conducts heat better (231 W/m·K vs 205 W/m·K). On the shop floor, 8017 welds better (excellent vs good) and 8011 sits in a lower cost tier (budget, $) than 8017 (standard, $$).
8011Choose it when strength drives the design, or when the part sees heat.
8017Choose it when the part is bent, formed or impact-loaded, or when it will be welded.
8011 vs 8017: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 69 GPa10 Msi · Shear Modulus 26 GPa3.8 Msi · Poisson's Ratio 0.33
Physical
Density and transition temperatures.
Melting Point (Solidus)
Liquidus Temperature
Same in both: Density 2.71 g/cm³0.1 lb/in³
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Specific Heat Capacity 900 J/kg·K0.21 BTU/lb·°F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.84 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Weldability
Formability (cold)
Polishability
Castability
Same in both: Machinability 30 / 100 · Machinability Rating (AISI 1212 = 100 %) 30% · Brazeability / Solderability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Water
Typical Recycled Content
Same in both: Embodied Energy (primary production) 200 MJ/kg85,985 BTU/lb · Embodied Carbon (primary production) 12 kg CO₂/kg
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Same in both: Specific Stiffness (E / density) 25.5 MN·m/kg
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 8011 | 8017 |
|---|---|---|
| Sheet metal | Yes | — |
| Default condition | — | — |
| Relative cost | $ Budget | $$ Standard |
| Min. machined wall | — | — |
| Best machined surface | — | — |
| Anodizing Type II | Yes | — |
| Cerakote | Yes | — |
| Chem Film (Alodine) | Yes | — |
| E-Coating | Yes | — |
| Electropolishing | Yes | — |
| Hard Anodize Type III w/ PTFE | Yes | — |
| Hard Anodizing Type III | Yes | — |
| Nickel Plating | Yes | — |
| PTFE Coating | Yes | — |
| Painting | Yes | — |
| Powder Coating | Yes | — |
They share 4 finishes: Electroless Nickel (EN), Epoxy Coating, Gold Plating, Silver Plating.
8011 vs 8017 — frequently asked
Is 8011 stronger than 8017?
Yes. 8011 has a typical yield strength of 120 MPa (17.4 ksi) against 95 MPa (13.8 ksi) for 8017 — about 26% more. Tensile strength is 145 MPa (21 ksi) vs 115 MPa (16.7 ksi).
Which is cheaper, 8011 or 8017?
8011 is the lower-cost material: it sits in the budget tier ($) while 8017 is standard ($$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which welds better, 8011 or 8017?
8017. Its weldability rates excellent (85/100) against good (60/100) for 8011.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 8011 and 8017 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.