Aluminum 8006 vs Sintered 2014
Aluminum · grade comparison
Aluminum 8006 and Sintered 2014 are both aluminum grades. Sintered 2014 is the stronger of the two: yield strength 250 MPa (36.3 ksi) against 130 MPa (18.9 ksi) for 8006, about 92% more; tensile strength follows at 270 MPa (39.2 ksi) vs 155 MPa (22.5 ksi). In exchange, 8006 is the more ductile: elongation 10% versus 1.5% for Sintered 2014, and Sintered 2014 is harder (90 HB vs 45 HB). Sintered 2014 is lighter (2.55 g/cm³ vs 2.71 g/cm³ for 8006) and 8006 is stiffer (69 GPa vs 62 GPa). On the shop floor, Sintered 2014 machines more easily (very good vs fair), 8006 welds better (very good vs poor), and 8006 sits in a lower cost tier (budget, $) than Sintered 2014 (high, $$$$).
8006Choose it when the part is bent, formed or impact-loaded, or when it will be welded.
Sintered 2014Choose it when strength drives the design, or when weight is the constraint.
8006 vs Sintered 2014: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Compressive Strength
Charpy V-Notch Impact (RT)
Hardness, Rockwell B
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Same in both: Latent Heat of Fusion 390 J/g168 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Brazeability / Solderability
Polishability
Castability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Typical Recycled Content
Same in both: Embodied Water 1,150 L/kg138 gal/lb
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 8006 | Sintered 2014 |
|---|---|---|
| Sheet metal | Yes | — |
| Default condition | — | — |
| Relative cost | $ Budget | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
| Anodizing Type II | Yes | — |
| Cerakote | Yes | — |
| Chem Film (Alodine) | Yes | — |
| E-Coating | Yes | — |
| Electropolishing | Yes | — |
| Hard Anodize Type III w/ PTFE | Yes | — |
| Hard Anodizing Type III | Yes | — |
| Nickel Plating | Yes | — |
| PTFE Coating | Yes | — |
| Painting | Yes | — |
| Powder Coating | Yes | — |
They share 4 finishes: Electroless Nickel (EN), Epoxy Coating, Gold Plating, Silver Plating.
8006 vs Sintered 2014 — frequently asked
Is Sintered 2014 stronger than 8006?
Yes. Sintered 2014 has a typical yield strength of 250 MPa (36.3 ksi) against 130 MPa (18.9 ksi) for 8006 — about 92% more. Tensile strength is 270 MPa (39.2 ksi) vs 155 MPa (22.5 ksi).
Which is cheaper, 8006 or Sintered 2014?
8006 is the lower-cost material: it sits in the budget tier ($) while Sintered 2014 is high ($$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, 8006 or Sintered 2014?
Sintered 2014. Its machinability rates very good (78/100) against fair (35/100) for 8006; for welding the order is 8006 first (very good, 70/100) then Sintered 2014 (poor, 18/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 8006 and Sintered 2014 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.