6262A-T4 and 6262A-T9 are two conditions of the same aluminum grade, 6262A: T4 (solution heat treated and naturally aged) versus T9 (solution heat treated, artificially aged and cold worked). The chemistry is identical, so every difference below comes from the condition. 6262A-T9 is the stronger of the two: yield strength 380 MPa (55.1 ksi) against 130 MPa (18.9 ksi) for 6262A-T4, about 192% more; tensile strength follows at 400 MPa (58 ksi) vs 240 MPa (34.8 ksi). In exchange, 6262A-T4 is the more ductile: elongation 20% versus 10% for 6262A-T9, and 6262A-T9 is harder (120 HB vs 65 HB). 6262A-T9 runs hotter in service (150°C vs 120°C continuous). On the shop floor, 6262A-T9 machines more easily (excellent vs very good).
6262A-T4Choose it when the part is bent, formed or impact-loaded.
6262A-T9Choose it when strength drives the design, or when the part sees heat.
6262A-T4 vs 6262A-T9: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Hardness, Brinell
Same in both: Elastic (Young's) Modulus 69.5 GPa10.1 Msi · Shear Modulus 26 GPa3.8 Msi · Bulk Modulus 68 GPa9.9 Msi · Poisson's Ratio 0.33
Physical
Density and transition temperatures.
Same in both: Density 2.71 g/cm³0.1 lb/in³ · Melting Point (Solidus) 582°C1,080 °F · Liquidus Temperature 652°C1,206 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 896 J/kg·K0.21 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 23.4 µm/m·K13 µin/in·°F · Latent Heat of Fusion 393 J/g169 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.76 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 25 / 100 · Polishability 60 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 205 MJ/kg88,134 BTU/lb · Embodied Carbon (primary production) 12.5 kg CO₂/kg · Embodied Water 1,200 L/kg144 gal/lb · Typical Recycled Content 25%
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
6262A-T4 vs 6262A-T9 — frequently asked
Is 6262A-T9 stronger than 6262A-T4?
Yes. 6262A-T9 has a typical yield strength of 380 MPa (55.1 ksi) against 130 MPa (18.9 ksi) for 6262A-T4 — about 192% more. Tensile strength is 400 MPa (58 ksi) vs 240 MPa (34.8 ksi).
Which condition does FabDigit quote by default, T4 or T9?
T6 is the default 6262A condition in the FabDigit quote flow (neither T4 nor T9). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 6262A-T4 or 6262A-T9?
6262A-T9. Its machinability rates excellent (95/100) against very good (78/100) for 6262A-T4; for welding the order is 6262A-T4 first (fair, 35/100) then 6262A-T9 (poor, 30/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 6262A-T4 and 6262A-T9 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.