Aluminum 6106-T1 vs 6106-T6
Aluminum · 6106 temper comparison
6106-T1 and 6106-T6 are two conditions of the same aluminum grade, 6106: T1 (cooled from hot working and naturally aged) versus T6 (solution heat treated and artificially aged). The chemistry is identical, so every difference below comes from the condition. 6106-T6 is the stronger of the two: yield strength 220 MPa (31.9 ksi) against 90 MPa (13.1 ksi) for 6106-T1, about 144% more; tensile strength follows at 265 MPa (38.4 ksi) vs 165 MPa (23.9 ksi). In exchange, 6106-T1 is the more ductile: elongation 16% versus 10% for 6106-T6, and 6106-T6 is harder (80 HB vs 50 HB). On the shop floor, 6106-T6 machines more easily (50 vs 38 out of 100).
6106-T1Choose it when the part is bent, formed or impact-loaded.
6106-T6Choose it when strength drives the design, or when the part is machined in volume.
6106-T1 vs 6106-T6: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 69.5 GPa10.1 Msi · Shear Modulus 26 GPa3.8 Msi · Bulk Modulus 69 GPa10 Msi · Poisson's Ratio 0.33
Physical
Density and transition temperatures.
Same in both: Density 2.7 g/cm³0.1 lb/in³ · Melting Point (Solidus) 615°C1,139 °F · Liquidus Temperature 655°C1,211 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Same in both: Specific Heat Capacity 900 J/kg·K0.21 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 23.4 µm/m·K13 µin/in·°F · Latent Heat of Fusion 393 J/g169 BTU/lb · Max Service Temperature (continuous) 150°C302 °F · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.82 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 45 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 200 MJ/kg85,985 BTU/lb · Embodied Carbon (primary production) 12.5 kg CO₂/kg · Embodied Water 1,100 L/kg132 gal/lb · Typical Recycled Content 35%
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
6106-T1 vs 6106-T6 — frequently asked
Is 6106-T6 stronger than 6106-T1?
Yes. 6106-T6 has a typical yield strength of 220 MPa (31.9 ksi) against 90 MPa (13.1 ksi) for 6106-T1 — about 144% more. Tensile strength is 265 MPa (38.4 ksi) vs 165 MPa (23.9 ksi).
Which condition does FabDigit quote by default, T1 or T6?
Specify the condition in the material field or the drawing note; FabDigit prices the quote for the state you call out.
Which is easier to machine, 6106-T1 or 6106-T6?
6106-T6, by a small margin. Both rate fair for machinability — 50/100 against 38/100 for 6106-T1; for welding the order is 6106-T1 first (excellent, 85/100) then 6106-T6 (very good, 80/100).