Aluminum 6061/Al2O3/20p-O vs 6061/Al2O3/20p-T6
Aluminum · 6061/Al2O3/20p temper comparison
6061/Al2O3/20p-O and 6061/Al2O3/20p-T6 are two conditions of the same aluminum grade, 6061/Al2O3/20p: O (annealed) versus T6 (solution heat treated and artificially aged). The chemistry is identical, so every difference below comes from the condition. 6061/Al2O3/20p-T6 is the stronger of the two: yield strength 317 MPa (46 ksi) against 75 MPa (10.9 ksi) for 6061/Al2O3/20p-O, about 4.2 times as much; tensile strength follows at 359 MPa (52.1 ksi) vs 150 MPa (21.8 ksi). In exchange, 6061/Al2O3/20p-O is the more ductile: elongation 10% versus 2.5% for 6061/Al2O3/20p-T6, and 6061/Al2O3/20p-T6 is harder (110 HB vs 48 HB). 6061/Al2O3/20p-O conducts electricity better (38 % IACS vs 32 % IACS).
6061/Al2O3/20p-OChoose it when the part is bent, formed or impact-loaded.
6061/Al2O3/20p-T6Choose it when strength drives the design.
6061/Al2O3/20p-O vs 6061/Al2O3/20p-T6: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
6061/Al2O3/20p-O6061/Al2O3/20p-T6
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Hardness, Brinell
Same in both: Elastic (Young's) Modulus 98 GPa14.2 Msi · Shear Modulus 38 GPa5.5 Msi · Bulk Modulus 90 GPa13.1 Msi · Poisson's Ratio 0.32 · Reduction in Area 3% · Compressive Strength 340 MPa49.3 ksi · Shear Strength 215 MPa31.2 ksi · Charpy V-Notch Impact (RT) 5 J3.7 ft·lbf · Hardness, Rockwell B 66 HRB · Hardness, Vickers 118 HV
Physical
Density and transition temperatures.
Same in both: Density 2.9 g/cm³0.1 lb/in³ · Melting Point (Solidus) 582°C1,080 °F · Liquidus Temperature 652°C1,206 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Same in both: Specific Heat Capacity 880 J/kg·K0.21 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 18 µm/m·K10 µin/in·°F · Latent Heat of Fusion 290 J/g125 BTU/lb · Max Service Temperature (continuous) 180°C356 °F · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Same in both: Electrical Resistivity 5.4×10⁻⁸ Ω·m2.13 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.8 V · Corrosion Resistance 55 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Formability (cold)
Same in both: Machinability Rating (AISI 1212 = 100 %) 20% · Weldability 35 / 100 · Castability 45 / 100 · Brazeability / Solderability 25 / 100 · Polishability 50 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 215 MJ/kg92,433 BTU/lb · Embodied Carbon (primary production) 13.5 kg CO₂/kg · Embodied Water 1,200 L/kg144 gal/lb · Typical Recycled Content 5%
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
6061/Al2O3/20p-O vs 6061/Al2O3/20p-T6 — frequently asked
Is 6061/Al2O3/20p-T6 stronger than 6061/Al2O3/20p-O?
Yes. 6061/Al2O3/20p-T6 has a typical yield strength of 317 MPa (46 ksi) against 75 MPa (10.9 ksi) for 6061/Al2O3/20p-O — about 4.2 times as much. Tensile strength is 359 MPa (52.1 ksi) vs 150 MPa (21.8 ksi).
Which condition does FabDigit quote by default, O or T6?
T6 is the default 6061/Al2O3/20p condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 6061/Al2O3/20p-O or 6061/Al2O3/20p-T6?
6061/Al2O3/20p-O, by a small margin. Both rate poor for machinability — 28/100 against 22/100 for 6061/Al2O3/20p-T6.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 6061/Al2O3/20p-O and 6061/Al2O3/20p-T6 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.