Aluminum 6005A vs 6162
Aluminum · grade comparison
Aluminum 6005A and 6162 are both aluminum grades. 6162 is the stronger of the two: yield strength 262 MPa (38 ksi) against 235 MPa (34.1 ksi) for 6005A, about 11% more; tensile strength follows at 290 MPa (42.1 ksi) vs 275 MPa (39.9 ksi). On the shop floor, 6005A sits in a lower cost tier (budget, $) than 6162 (standard, $$).
6005AChoose it when cost is the deciding factor.
6162Choose it when strength drives the design.
6005A vs 6162: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Same in both: Shear Modulus 26 GPa3.8 Msi · Bulk Modulus 69 GPa10 Msi · Poisson's Ratio 0.33 · Fracture Toughness (K_IC) 29 MPa·√m26.4 ksi·√in · Hardness, Brinell 95 HB · Hardness, Vickers 100 HV
Physical
Density and transition temperatures.
Melting Point (Solidus)
Liquidus Temperature
Same in both: Density 2.7 g/cm³0.1 lb/in³
Thermal
How each material carries heat and how hot it can run.
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Same in both: Thermal Conductivity 190 W/m·K110 BTU/hr·ft·°F · Latent Heat of Fusion 393 J/g169 BTU/lb · Max Service Temperature (continuous) 150°C302 °F · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Same in both: Corrosion Resistance 68 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Formability (cold)
Castability
Polishability
Same in both: Machinability Rating (AISI 1212 = 100 %) 190% · Brazeability / Solderability 45 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Water
Same in both: Embodied Carbon (primary production) 12.5 kg CO₂/kg · Typical Recycled Content 30%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Shock Resistance Index
Same in both: Thermal Diffusivity 78.5 mm²/s
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 6005A | 6162 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $ Budget | $$ Standard |
| Min. machined wall | 0.5 mm | 0.5 mm |
| Best machined surface | Ra 0.8 µm | Ra 0.8 µm |
Both are offered for CNC machining and Sheet metal. Both take the same 16 finishes: Anodizing Type II, Cerakote, Chem Film (Alodine), DLC, E-Coating, Electroless Nickel (EN), Electropolishing, Epoxy Coating, Gold Plating, Hard Anodize Type III w/ PTFE, Hard Anodizing Type III, Nickel Plating and 4 more.
6005A vs 6162 — frequently asked
Is 6162 stronger than 6005A?
Yes. 6162 has a typical yield strength of 262 MPa (38 ksi) against 235 MPa (34.1 ksi) for 6005A — about 11% more. Tensile strength is 290 MPa (42.1 ksi) vs 275 MPa (39.9 ksi).
Which is cheaper, 6005A or 6162?
6005A is the lower-cost material: it sits in the budget tier ($) while 6162 is standard ($$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which welds better, 6005A or 6162?
6005A. Its weldability rates excellent (85/100) against very good (80/100) for 6162.