Aluminum 5449-H111 vs 5449-H28
Aluminum · 5449 temper comparison
5449-H111 and 5449-H28 are two conditions of the same aluminum grade, 5449: H111 (slightly strain hardened) versus H28 (strain hardened and partially annealed, full hard). The chemistry is identical, so every difference below comes from the condition. 5449-H28 is the stronger of the two: yield strength 260 MPa (37.7 ksi) against 100 MPa (14.5 ksi) for 5449-H111, about 160% more; tensile strength follows at 305 MPa (44.2 ksi) vs 215 MPa (31.2 ksi). In exchange, 5449-H111 is the more ductile: elongation 22% versus 4% for 5449-H28, and 5449-H28 is harder (88 HB vs 58 HB). 5449-H111 runs hotter in service (150°C vs 100°C continuous). On the shop floor, 5449-H28 machines more easily (fair vs poor) and 5449-H111 welds better (excellent vs very good).
5449-H111Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
5449-H28Choose it when strength drives the design, or when the part is machined in volume.
5449-H111 vs 5449-H28: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Same in both: Elastic (Young's) Modulus 70 GPa10.2 Msi · Shear Modulus 26.4 GPa3.8 Msi · Bulk Modulus 69 GPa10 Msi · Poisson's Ratio 0.33
Physical
Density and transition temperatures.
Same in both: Density 2.68 g/cm³0.1 lb/in³ · Melting Point (Solidus) 610°C1,130 °F · Liquidus Temperature 652°C1,206 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 137 W/m·K79.2 BTU/hr·ft·°F · Specific Heat Capacity 900 J/kg·K0.21 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 23.7 µm/m·K13.2 µin/in·°F · Latent Heat of Fusion 395 J/g170 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Same in both: Electrical Resistivity 5.2×10⁻⁸ Ω·m2.05 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.85 V · Corrosion Resistance 74 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 30 / 100 · Brazeability / Solderability 25 / 100 · Polishability 60 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 200 MJ/kg85,985 BTU/lb · Embodied Carbon (primary production) 12 kg CO₂/kg · Embodied Water 1,150 L/kg138 gal/lb · Typical Recycled Content 35%
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
5449-H111 vs 5449-H28 — frequently asked
Is 5449-H28 stronger than 5449-H111?
Yes. 5449-H28 has a typical yield strength of 260 MPa (37.7 ksi) against 100 MPa (14.5 ksi) for 5449-H111 — about 160% more. Tensile strength is 305 MPa (44.2 ksi) vs 215 MPa (31.2 ksi).
Which condition does FabDigit quote by default, H111 or H28?
O is the default 5449 condition in the FabDigit quote flow (neither H111 nor H28). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 5449-H111 or 5449-H28?
5449-H28. Its machinability rates fair (50/100) against poor (34/100) for 5449-H111; for welding the order is 5449-H111 first (excellent, 90/100) then 5449-H28 (very good, 80/100).