Aluminum 5352-H112 vs 5352-H14
Aluminum · 5352 temper comparison
5352-H112 and 5352-H14 are two conditions of the same aluminum grade, 5352: H112 (strain hardened from hot working only) versus H14 (strain hardened, half hard). The chemistry is identical, so every difference below comes from the condition. 5352-H14 is the stronger of the two: yield strength 215 MPa (31.2 ksi) against 110 MPa (16 ksi) for 5352-H112, about 95% more; tensile strength follows at 260 MPa (37.7 ksi) vs 200 MPa (29 ksi). In exchange, 5352-H112 is the more ductile: elongation 18% versus 10% for 5352-H14, and 5352-H14 is harder (68 HB vs 50 HB). 5352-H112 runs hotter in service (150°C vs 120°C continuous). On the shop floor, 5352-H14 machines more easily (45 vs 35 out of 100).
5352-H112Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
5352-H14Choose it when strength drives the design, or when the part is machined in volume.
5352-H112 vs 5352-H14: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Same in both: Elastic (Young's) Modulus 70.3 GPa10.2 Msi · Shear Modulus 25.9 GPa3.8 Msi · Bulk Modulus 69 GPa10 Msi · Poisson's Ratio 0.33
Physical
Density and transition temperatures.
Same in both: Density 2.68 g/cm³0.1 lb/in³ · Melting Point (Solidus) 607°C1,125 °F · Liquidus Temperature 650°C1,202 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 900 J/kg·K0.21 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 23.8 µm/m·K13.2 µin/in·°F · Latent Heat of Fusion 397 J/g171 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 35 % IACS · Electrical Resistivity 4.9×10⁻⁸ Ω·m1.93 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.85 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 25 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 200 MJ/kg85,985 BTU/lb · Embodied Carbon (primary production) 12 kg CO₂/kg · Embodied Water 1,200 L/kg144 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
5352-H112 vs 5352-H14 — frequently asked
Is 5352-H14 stronger than 5352-H112?
Yes. 5352-H14 has a typical yield strength of 215 MPa (31.2 ksi) against 110 MPa (16 ksi) for 5352-H112 — about 95% more. Tensile strength is 260 MPa (37.7 ksi) vs 200 MPa (29 ksi).
Which condition does FabDigit quote by default, H112 or H14?
Specify the condition in the material field or the drawing note; FabDigit prices the quote for the state you call out.
Which is easier to machine, 5352-H112 or 5352-H14?
5352-H14, by a small margin. Both rate fair for machinability — 45/100 against 35/100 for 5352-H112.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 5352-H112 and 5352-H14 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.