Aluminum 5050 vs 5A05
Aluminum · grade comparison
Aluminum 5050 and 5A05 are both aluminum grades. 5A05 is the stronger of the two: tensile strength 270 MPa (39.2 ksi) against 170 MPa (24.7 ksi) for 5050, about 59% more. 5A05 is the more ductile: elongation 22% versus 9% for 5050, and 5A05 is harder (70 HB vs 46 HB). 5050 runs hotter in service (150°C vs 65°C continuous) and 5050 conducts heat better (191 W/m·K vs 117 W/m·K). On the shop floor, 5050 sits in a lower cost tier (budget, $) than 5A05 (premium, $$$).
5050Choose it when the part sees heat, or when cost is the deciding factor.
5A05Choose it when strength drives the design, or when the part is bent, formed or impact-loaded.
5050 vs 5A05: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Fracture Toughness (K_IC)
Same in both: Poisson's Ratio 0.33 · Yield Strength (0.2% offset) 145 MPa21 ksi
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Latent Heat of Fusion
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 900 J/kg·K0.21 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 23.8 µm/m·K13.2 µin/in·°F · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Same in both: Corrosion Resistance 75 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Weldability
Formability (cold)
Brazeability / Solderability
Polishability
Same in both: Machinability 40 / 100 · Machinability Rating (AISI 1212 = 100 %) 30%
Sustainability
Primary-production footprint per kilogram.
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Same in both: Embodied Energy (primary production) 200 MJ/kg85,985 BTU/lb
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 5050 | 5A05 |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Default condition | — | — |
| Relative cost | $ Budget | $$$ Premium |
| Min. machined wall | 0.5 mm | — |
| Best machined surface | Ra 0.8 µm | — |
| Anodizing Type II | Yes | — |
| Cerakote | Yes | — |
| Chem Film (Alodine) | Yes | — |
| DLC | Yes | — |
| E-Coating | Yes | — |
| Electropolishing | Yes | — |
| Hard Anodize Type III w/ PTFE | Yes | — |
| Hard Anodizing Type III | Yes | — |
| Nickel Plating | Yes | — |
| PTFE Coating | Yes | — |
| Painting | Yes | — |
| Powder Coating | Yes | — |
They share 4 finishes: Electroless Nickel (EN), Epoxy Coating, Gold Plating, Silver Plating.
5050 vs 5A05 — frequently asked
Is 5A05 stronger than 5050?
Yes. 5A05 has a typical tensile strength of 270 MPa (39.2 ksi) against 170 MPa (24.7 ksi) for 5050 — about 59% more.
Which is cheaper, 5050 or 5A05?
5050 is the lower-cost material: it sits in the budget tier ($) while 5A05 is premium ($$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which welds better, 5050 or 5A05?
5A05. Its weldability rates excellent (90/100) against excellent (85/100) for 5050.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 5050 and 5A05 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.