Aluminum 344.0-T6 vs 344.0-T7
Aluminum · 344.0 temper comparison
344.0-T6 and 344.0-T7 are two conditions of the same aluminum grade, 344.0: T6 (solution heat treated and artificially aged) versus T7 (solution heat treated and overaged (stabilized)). The chemistry is identical, so every difference below comes from the condition. 344.0-T6 is the stronger of the two: yield strength 210 MPa (30.5 ksi) against 190 MPa (27.6 ksi) for 344.0-T7, about 11% more; tensile strength follows at 285 MPa (41.3 ksi) vs 250 MPa (36.3 ksi). In exchange, 344.0-T7 is the more ductile: elongation 2% versus 1.5% for 344.0-T6, and 344.0-T6 is harder (105 HB vs 90 HB). 344.0-T7 runs hotter in service (200°C vs 175°C continuous) and 344.0-T7 conducts heat better (120 W/m·K vs 105 W/m·K).
344.0-T6Choose it when strength drives the design.
344.0-T7Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
344.0-T6 vs 344.0-T7: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Same in both: Elastic (Young's) Modulus 74 GPa10.7 Msi · Shear Modulus 28 GPa4.1 Msi · Bulk Modulus 72 GPa10.4 Msi · Poisson's Ratio 0.33 · Compressive Strength 130 MPa18.9 ksi · Fracture Toughness (K_IC) 17 MPa·√m15.5 ksi·√in · Charpy V-Notch Impact (RT) 4 J3 ft·lbf
Physical
Density and transition temperatures.
Same in both: Density 2.75 g/cm³0.1 lb/in³ · Melting Point (Solidus) 521°C970 °F · Liquidus Temperature 582°C1,080 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 963 J/kg·K0.23 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 21 µm/m·K11.7 µin/in·°F · Latent Heat of Fusion 389 J/g167 BTU/lb · Min Service Temperature -100°C-148 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Same in both: Electrical Resistivity 6.2×10⁻⁸ Ω·m2.44 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.83 V · Corrosion Resistance 40 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Same in both: Machinability Rating (AISI 1212 = 100 %) 70% · Weldability 40 / 100 · Formability (cold) 5 / 100 · Castability 88 / 100 · Brazeability / Solderability 20 / 100 · Polishability 45 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 155 MJ/kg66,638 BTU/lb · Embodied Carbon (primary production) 9.5 kg CO₂/kg · Embodied Water 900 L/kg108 gal/lb · Typical Recycled Content 75%
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
344.0-T6 vs 344.0-T7 — frequently asked
Is 344.0-T6 stronger than 344.0-T7?
Yes. 344.0-T6 has a typical yield strength of 210 MPa (30.5 ksi) against 190 MPa (27.6 ksi) for 344.0-T7 — about 11% more. Tensile strength is 285 MPa (41.3 ksi) vs 250 MPa (36.3 ksi).
Which condition does FabDigit quote by default, T6 or T7?
F is the default 344.0 condition in the FabDigit quote flow (neither T6 nor T7). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose 344.0-T6 over 344.0-T7?
Pick 344.0-T6 when strength drives the design. Pick 344.0-T7 when the part is bent, formed or impact-loaded, or when the part sees heat.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 344.0-T6 and 344.0-T7 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.