Aluminum 319 vs A390
Aluminum · grade comparison
Aluminum 319 and A390 are both aluminum grades, both cast al. A390 is the stronger of the two: yield strength 240 MPa (34.8 ksi) against 124 MPa (18 ksi) for 319, about 94% more; tensile strength follows at 280 MPa (40.6 ksi) vs 186 MPa (27 ksi). In exchange, 319 is the more ductile: elongation 2% versus 1% for A390, and A390 is harder (120 HB vs 70 HB). A390 is stiffer (81 GPa vs 74 GPa) and A390 conducts heat better (134 W/m·K vs 109 W/m·K). On the shop floor, 319 machines more easily (very good vs poor), 319 welds better (good vs poor), and 319 sits in a lower cost tier (budget, $) than A390 (standard, $$).
319Choose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
A390Choose it when strength drives the design.
319 vs A390: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Compressive Strength
Hardness, Vickers
Same in both: Poisson's Ratio 0.33
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Same in both: Specific Heat Capacity 963 J/kg·K0.23 BTU/lb·°F · Max Service Temperature (continuous) 200°C392 °F · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.78 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Same in both: Polishability 40 / 100
Sustainability
Primary-production footprint per kilogram.
Typical Recycled Content
Same in both: Embodied Energy (primary production) 200 MJ/kg85,985 BTU/lb · Embodied Carbon (primary production) 12 kg CO₂/kg · Embodied Water 1,200 L/kg144 gal/lb
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 319 | A390 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $ Budget | $$ Standard |
| Min. machined wall | 0.5 mm | 0.5 mm |
| Best machined surface | Ra 0.8 µm | Ra 0.8 µm |
Both are offered for CNC machining. Both take the same 16 finishes: Anodizing Type II, Cerakote, Chem Film (Alodine), DLC, E-Coating, Electroless Nickel (EN), Electropolishing, Epoxy Coating, Gold Plating, Hard Anodize Type III w/ PTFE, Hard Anodizing Type III, Nickel Plating and 4 more.
319 vs A390 — frequently asked
Is A390 stronger than 319?
Yes. A390 has a typical yield strength of 240 MPa (34.8 ksi) against 124 MPa (18 ksi) for 319 — about 94% more. Tensile strength is 280 MPa (40.6 ksi) vs 186 MPa (27 ksi).
Which is cheaper, 319 or A390?
319 is the lower-cost material: it sits in the budget tier ($) while A390 is standard ($$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, 319 or A390?
319. Its machinability rates very good (72/100) against poor (30/100) for A390; for welding the order is 319 first (good, 55/100) then A390 (poor, 20/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 319 and A390 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.