Aluminum 319 vs 359.0
Aluminum · grade comparison
Aluminum 319 and 359.0 are both aluminum grades. 359.0 is the stronger of the two: yield strength 250 MPa (36.3 ksi) against 124 MPa (18 ksi) for 319, about 102% more; tensile strength follows at 325 MPa (47.1 ksi) vs 186 MPa (27 ksi). 359.0 is the more ductile: elongation 5% versus 2% for 319, and 359.0 is harder (80 HB vs 70 HB). 359.0 is lighter (2.67 g/cm³ vs 2.79 g/cm³ for 319) and 319 runs hotter in service (200°C vs 150°C continuous). On the shop floor, 319 machines more easily (very good vs good), 359.0 welds better (65 vs 55 out of 100), and 319 sits in a lower cost tier (budget, $) than 359.0 (standard, $$).
319Choose it when the part sees heat, or when the part is machined in volume.
359.0Choose it when strength drives the design, or when the part is bent, formed or impact-loaded.
319 vs 359.0: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Same in both: Poisson's Ratio 0.33
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 963 J/kg·K0.23 BTU/lb·°F · Latent Heat of Fusion 389 J/g167 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Brazeability / Solderability
Polishability
Same in both: Castability 90 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Same in both: Embodied Energy (primary production) 200 MJ/kg85,985 BTU/lb
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 319 | 359.0 |
|---|---|---|
| CNC machining | Yes | — |
| Default condition | — | — |
| Relative cost | $ Budget | $$ Standard |
| Min. machined wall | 0.5 mm | — |
| Best machined surface | Ra 0.8 µm | — |
| Anodizing Type II | Yes | — |
| Cerakote | Yes | — |
| Chem Film (Alodine) | Yes | — |
| DLC | Yes | — |
| E-Coating | Yes | — |
| Electropolishing | Yes | — |
| Hard Anodize Type III w/ PTFE | Yes | — |
| Hard Anodizing Type III | Yes | — |
| Nickel Plating | Yes | — |
| PTFE Coating | Yes | — |
| Painting | Yes | — |
| Powder Coating | Yes | — |
They share 4 finishes: Electroless Nickel (EN), Epoxy Coating, Gold Plating, Silver Plating.
319 vs 359.0 — frequently asked
Is 359.0 stronger than 319?
Yes. 359.0 has a typical yield strength of 250 MPa (36.3 ksi) against 124 MPa (18 ksi) for 319 — about 102% more. Tensile strength is 325 MPa (47.1 ksi) vs 186 MPa (27 ksi).
Which is cheaper, 319 or 359.0?
319 is the lower-cost material: it sits in the budget tier ($) while 359.0 is standard ($$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, 319 or 359.0?
319. Its machinability rates very good (72/100) against good (55/100) for 359.0; for welding the order is 359.0 first (good, 65/100) then 319 (good, 55/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 319 and 359.0 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.