Aluminum 2A17-T4 vs 2A17-T651
Aluminum · 2A17 temper comparison
2A17-T4 and 2A17-T651 are two conditions of the same aluminum grade, 2A17: T4 (solution heat treated and naturally aged) versus T651 (T6, stress relieved by stretching). The chemistry is identical, so every difference below comes from the condition. 2A17-T651 is the stronger of the two: yield strength 315 MPa (45.7 ksi) against 235 MPa (34.1 ksi) for 2A17-T4, about 34% more; tensile strength follows at 430 MPa (62.4 ksi) vs 380 MPa (55.1 ksi). In exchange, 2A17-T4 is the more ductile: elongation 14% versus 8% for 2A17-T651, and 2A17-T651 is harder (118 HB vs 100 HB). 2A17-T651 runs hotter in service (250°C vs 150°C continuous) and 2A17-T651 conducts electricity better (35 % IACS vs 30 % IACS).
2A17-T4Choose it when the part is bent, formed or impact-loaded.
2A17-T651Choose it when strength drives the design, or when the part sees heat.
2A17-T4 vs 2A17-T651: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fracture Toughness (K_IC)
Hardness, Brinell
Same in both: Elastic (Young's) Modulus 72 GPa10.4 Msi · Shear Modulus 27 GPa3.9 Msi · Bulk Modulus 71 GPa10.3 Msi · Poisson's Ratio 0.33 · Fatigue Strength (Endurance Limit) 120 MPa17.4 ksi
Physical
Density and transition temperatures.
Same in both: Density 2.84 g/cm³0.1 lb/in³ · Melting Point (Solidus) 540°C1,004 °F · Liquidus Temperature 650°C1,202 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 870 J/kg·K0.21 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 22.6 µm/m·K12.6 µin/in·°F · Latent Heat of Fusion 390 J/g168 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Same in both: Electrical Resistivity 4.9×10⁻⁸ Ω·m1.93 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.69 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Weldability 58 / 100 · Castability 25 / 100 · Brazeability / Solderability 15 / 100 · Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 200 MJ/kg85,985 BTU/lb · Embodied Carbon (primary production) 12.5 kg CO₂/kg · Embodied Water 1,200 L/kg144 gal/lb · Typical Recycled Content 10%
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
2A17-T4 vs 2A17-T651 — frequently asked
Is 2A17-T651 stronger than 2A17-T4?
Yes. 2A17-T651 has a typical yield strength of 315 MPa (45.7 ksi) against 235 MPa (34.1 ksi) for 2A17-T4 — about 34% more. Tensile strength is 430 MPa (62.4 ksi) vs 380 MPa (55.1 ksi).
Which condition does FabDigit quote by default, T4 or T651?
T6 is the default 2A17 condition in the FabDigit quote flow (neither T4 nor T651). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 2A17-T4 or 2A17-T651?
2A17-T651. Its machinability rates very good (74/100) against good (65/100) for 2A17-T4.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 2A17-T4 and 2A17-T651 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.