2419-O and 2419-T851 are two conditions of the same aluminum grade, 2419: O (annealed) versus T851 (T8, stress relieved by stretching). The chemistry is identical, so every difference below comes from the condition. 2419-T851 is the stronger of the two: yield strength 350 MPa (50.8 ksi) against 76 MPa (11 ksi) for 2419-O, about 4.6 times as much; tensile strength follows at 455 MPa (66 ksi) vs 172 MPa (24.9 ksi). In exchange, 2419-O is the more ductile: elongation 18% versus 10% for 2419-T851, and 2419-T851 is harder (130 HB vs 46 HB). 2419-O runs hotter in service (200°C vs 175°C continuous) and 2419-O conducts heat better (170 W/m·K vs 120 W/m·K). On the shop floor, 2419-T851 machines more easily (very good vs fair).
2419-OChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
2419-T851Choose it when strength drives the design, or when the part is machined in volume.
2419-O vs 2419-T851: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Same in both: Shear Modulus 27 GPa3.9 Msi · Bulk Modulus 75 GPa10.9 Msi · Poisson's Ratio 0.33 · Fracture Toughness (K_IC) 40 MPa·√m36.4 ksi·√in · Hardness, Rockwell B 78 HRB
Physical
Density and transition temperatures.
Same in both: Density 2.84 g/cm³0.1 lb/in³ · Melting Point (Solidus) 543°C1,009 °F · Liquidus Temperature 643°C1,189 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 864 J/kg·K0.21 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 22.3 µm/m·K12.4 µin/in·°F · Latent Heat of Fusion 389 J/g167 BTU/lb · Min Service Temperature -253°C-423 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.8 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 15 / 100 · Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 205 MJ/kg88,134 BTU/lb · Embodied Carbon (primary production) 12.5 kg CO₂/kg · Embodied Water 1,200 L/kg144 gal/lb · Typical Recycled Content 5%
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
2419-O vs 2419-T851 — frequently asked
Is 2419-T851 stronger than 2419-O?
Yes. 2419-T851 has a typical yield strength of 350 MPa (50.8 ksi) against 76 MPa (11 ksi) for 2419-O — about 4.6 times as much. Tensile strength is 455 MPa (66 ksi) vs 172 MPa (24.9 ksi).
Which condition does FabDigit quote by default, O or T851?
T851 is the default 2419 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 2419-O or 2419-T851?
2419-T851. Its machinability rates very good (75/100) against fair (45/100) for 2419-O; for welding the order is 2419-O first (very good, 78/100) then 2419-T851 (very good, 72/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 2419-O and 2419-T851 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.