Aluminum 2319-H14 vs 2319-T4
Aluminum · 2319 temper comparison
2319-H14 and 2319-T4 are two conditions of the same aluminum grade, 2319: H14 (strain hardened, half hard) versus T4 (solution heat treated and naturally aged). The chemistry is identical, so every difference below comes from the condition. 2319-T4 is the stronger of the two: tensile strength 330 MPa (47.9 ksi) against 260 MPa (37.7 ksi) for 2319-H14, about 27% more. 2319-T4 is the more ductile: elongation 16% versus 8% for 2319-H14, and 2319-T4 is harder (95 HB vs 78 HB). 2319-T4 runs hotter in service (175°C vs 150°C continuous) and 2319-H14 conducts heat better (165 W/m·K vs 116 W/m·K).
2319-T4Choose it when strength drives the design, or when the part is bent, formed or impact-loaded.
2319-H14 vs 2319-T4: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Hardness, Brinell
Same in both: Elastic (Young's) Modulus 73 GPa10.6 Msi · Shear Modulus 27 GPa3.9 Msi · Bulk Modulus 75 GPa10.9 Msi · Poisson's Ratio 0.33
Physical
Density and transition temperatures.
Same in both: Density 2.84 g/cm³0.1 lb/in³ · Melting Point (Solidus) 543°C1,009 °F · Liquidus Temperature 643°C1,189 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 864 J/kg·K0.21 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 22.3 µm/m·K12.4 µin/in·°F · Latent Heat of Fusion 385 J/g166 BTU/lb · Min Service Temperature -253°C-423 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.64 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Formability (cold)
Same in both: Machinability Rating (AISI 1212 = 100 %) 55% · Weldability 92 / 100 · Castability 60 / 100 · Brazeability / Solderability 20 / 100 · Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 205 MJ/kg88,134 BTU/lb · Embodied Carbon (primary production) 12.5 kg CO₂/kg · Embodied Water 1,150 L/kg138 gal/lb · Typical Recycled Content 10%
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
2319-H14 vs 2319-T4 — frequently asked
Is 2319-T4 stronger than 2319-H14?
Yes. 2319-T4 has a typical tensile strength of 330 MPa (47.9 ksi) against 260 MPa (37.7 ksi) for 2319-H14 — about 27% more.
Which condition does FabDigit quote by default, H14 or T4?
Specify the condition in the material field or the drawing note; FabDigit prices the quote for the state you call out.
When should I choose 2319-H14 over 2319-T4?
Pick 2319-T4 when strength drives the design, or when the part is bent, formed or impact-loaded.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 2319-H14 and 2319-T4 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.