Aluminum 2094-O vs 2094-T6
Aluminum · 2094 temper comparison
2094-O and 2094-T6 are two conditions of the same aluminum grade, 2094: O (annealed) versus T6 (solution heat treated and artificially aged). The chemistry is identical, so every difference below comes from the condition. 2094-T6 is the stronger of the two: yield strength 505 MPa (73.2 ksi) against 135 MPa (19.6 ksi) for 2094-O, about 3.7 times as much; tensile strength follows at 565 MPa (81.9 ksi) vs 250 MPa (36.3 ksi). In exchange, 2094-O is the more ductile: elongation 16% versus 6% for 2094-T6, and 2094-T6 is harder (158 HB vs 65 HB). 2094-O conducts heat better (125 W/m·K vs 95 W/m·K). On the shop floor, 2094-T6 machines more easily (good vs fair).
2094-OChoose it when the part is bent, formed or impact-loaded.
2094-T6Choose it when strength drives the design, or when the part is machined in volume.
2094-O vs 2094-T6: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Hardness, Brinell
Hardness, Vickers
Same in both: Shear Modulus 29.5 GPa4.3 Msi · Bulk Modulus 76 GPa11 Msi · Poisson's Ratio 0.33
Physical
Density and transition temperatures.
Same in both: Density 2.6 g/cm³0.09 lb/in³ · Melting Point (Solidus) 530°C986 °F · Liquidus Temperature 640°C1,184 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Same in both: Specific Heat Capacity 900 J/kg·K0.21 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 21.8 µm/m·K12.1 µin/in·°F · Latent Heat of Fusion 390 J/g168 BTU/lb · Max Service Temperature (continuous) 150°C302 °F · Min Service Temperature -253°C-423 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.78 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 10 / 100 · Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 215 MJ/kg92,433 BTU/lb · Embodied Carbon (primary production) 13 kg CO₂/kg · Embodied Water 1,200 L/kg144 gal/lb · Typical Recycled Content 5%
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
2094-O vs 2094-T6 — frequently asked
Is 2094-T6 stronger than 2094-O?
Yes. 2094-T6 has a typical yield strength of 505 MPa (73.2 ksi) against 135 MPa (19.6 ksi) for 2094-O — about 3.7 times as much. Tensile strength is 565 MPa (81.9 ksi) vs 250 MPa (36.3 ksi).
Which condition does FabDigit quote by default, O or T6?
T861 is the default 2094 condition in the FabDigit quote flow (neither O nor T6). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 2094-O or 2094-T6?
2094-T6. Its machinability rates good (60/100) against fair (45/100) for 2094-O; for welding the order is 2094-O first (good, 60/100) then 2094-T6 (good, 55/100).