Aluminum 2014-T351 vs 2014-T6
Aluminum · 2014 temper comparison
2014-T351 and 2014-T6 are two conditions of the same aluminum grade, 2014: T351 (T3, stress relieved by stretching) versus T6 (solution heat treated and artificially aged). The chemistry is identical, so every difference below comes from the condition. 2014-T6 is the stronger of the two: yield strength 414 MPa (60 ksi) against 295 MPa (42.8 ksi) for 2014-T351, about 40% more; tensile strength follows at 483 MPa (70.1 ksi) vs 440 MPa (63.8 ksi). In exchange, 2014-T351 is the more ductile: elongation 18% versus 13% for 2014-T6, and 2014-T6 is harder (135 HB vs 105 HB). 2014-T6 runs hotter in service (150°C vs 120°C continuous) and 2014-T6 conducts heat better (155 W/m·K vs 134 W/m·K).
2014-T351Choose it when the part is bent, formed or impact-loaded.
2014-T6Choose it when strength drives the design, or when the part sees heat.
2014-T351 vs 2014-T6: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 72.4 GPa10.5 Msi · Shear Modulus 28 GPa4.1 Msi · Bulk Modulus 71 GPa10.3 Msi · Poisson's Ratio 0.33
Physical
Density and transition temperatures.
Same in both: Density 2.8 g/cm³0.1 lb/in³ · Melting Point (Solidus) 507°C945 °F · Liquidus Temperature 638°C1,180 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Min Service Temperature
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Polishability
Same in both: Castability 25 / 100 · Brazeability / Solderability 15 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Same in both: Typical Recycled Content 20%
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
2014-T351 vs 2014-T6 — frequently asked
Is 2014-T6 stronger than 2014-T351?
Yes. 2014-T6 has a typical yield strength of 414 MPa (60 ksi) against 295 MPa (42.8 ksi) for 2014-T351 — about 40% more. Tensile strength is 483 MPa (70.1 ksi) vs 440 MPa (63.8 ksi).
Which condition does FabDigit quote by default, T351 or T6?
Specify the condition in the material field or the drawing note; FabDigit prices the quote for the state you call out.
Which welds better, 2014-T351 or 2014-T6?
2014-T6. Its weldability rates poor (25/100) against poor (20/100) for 2014-T351.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 2014-T351 and 2014-T6 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.