Aluminum 2011A-T4 vs 2011A-T8
Aluminum · 2011A temper comparison
2011A-T4 and 2011A-T8 are two conditions of the same aluminum grade, 2011A: T4 (solution heat treated and naturally aged) versus T8 (solution heat treated, cold worked and artificially aged). The chemistry is identical, so every difference below comes from the condition. 2011A-T8 is the stronger of the two: yield strength 310 MPa (45 ksi) against 215 MPa (31.2 ksi) for 2011A-T4, about 44% more; tensile strength follows at 405 MPa (58.7 ksi) vs 330 MPa (47.9 ksi). In exchange, 2011A-T4 is the more ductile: elongation 18% versus 12% for 2011A-T8, and 2011A-T8 is harder (100 HB vs 85 HB). 2011A-T8 runs hotter in service (130°C vs 100°C continuous) and 2011A-T8 conducts heat better (172 W/m·K vs 152 W/m·K).
2011A-T4Choose it when the part is bent, formed or impact-loaded.
2011A-T8Choose it when strength drives the design, or when the part sees heat.
2011A-T4 vs 2011A-T8: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 70 GPa10.2 Msi · Shear Modulus 26 GPa3.8 Msi · Bulk Modulus 69 GPa10 Msi · Poisson's Ratio 0.33
Physical
Density and transition temperatures.
Same in both: Density 2.83 g/cm³0.1 lb/in³ · Melting Point (Solidus) 535°C995 °F · Liquidus Temperature 643°C1,189 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 864 J/kg·K0.21 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 22.9 µm/m·K12.7 µin/in·°F · Latent Heat of Fusion 390 J/g168 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.72 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Formability (cold)
Same in both: Machinability Rating (AISI 1212 = 100 %) 300% · Weldability 10 / 100 · Castability 25 / 100 · Brazeability / Solderability 10 / 100 · Polishability 45 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 200 MJ/kg85,985 BTU/lb · Embodied Carbon (primary production) 12.5 kg CO₂/kg · Embodied Water 1,100 L/kg132 gal/lb · Typical Recycled Content 25%
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
2011A-T4 vs 2011A-T8 — frequently asked
Is 2011A-T8 stronger than 2011A-T4?
Yes. 2011A-T8 has a typical yield strength of 310 MPa (45 ksi) against 215 MPa (31.2 ksi) for 2011A-T4 — about 44% more. Tensile strength is 405 MPa (58.7 ksi) vs 330 MPa (47.9 ksi).
Which condition does FabDigit quote by default, T4 or T8?
T3 is the default 2011A condition in the FabDigit quote flow (neither T4 nor T8). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 2011A-T4 or 2011A-T8?
2011A-T8, by a small margin. Both rate excellent for machinability — 100/100 against 95/100 for 2011A-T4.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 2011A-T4 and 2011A-T8 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.