Tungsten Alloy EWTh-2 vs W-25Re
Tungsten Alloy · grade comparison
Tungsten Alloy EWTh-2 and W-25Re are both tungsten alloy grades. W-25Re is the stronger of the two: yield strength 1,850 MPa (268 ksi) against 1,150 MPa (167 ksi) for EWTh-2, about 61% more; tensile strength follows at 2,100 MPa (305 ksi) vs 1,400 MPa (203 ksi). W-25Re is the more ductile: elongation 4% versus 2% for EWTh-2, and W-25Re is harder (620 HV vs 470 HV). EWTh-2 is lighter (19.1 g/cm³ vs 19.7 g/cm³ for W-25Re) and EWTh-2 conducts heat better (125 W/m·K vs 45 W/m·K). On the shop floor, W-25Re welds better (fair vs not recommended).
EWTh-2Choose it when weight is the constraint.
W-25ReChoose it when strength drives the design, or when the part is bent, formed or impact-loaded.
EWTh-2 vs W-25Re: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all tungsten alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all tungsten alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Rockwell C
Hardness, Vickers
Reduction in Area
Fatigue Strength (Endurance Limit)
Same in both: Elastic (Young's) Modulus 400 GPa58 Msi · Shear Modulus 156 GPa22.6 Msi · Bulk Modulus 310 GPa45 Msi
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Min Service Temperature
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.15 V · Corrosion Resistance 60 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Weldability
Formability (cold)
Brazeability / Solderability
Polishability
Same in both: Machinability 8 / 100 · Machinability Rating (AISI 1212 = 100 %) 5%
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Typical Recycled Content
Same in both: Embodied Water 400 L/kg47.9 gal/lb
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every tungsten alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | EWTh-2 | W-25Re |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
EWTh-2 vs W-25Re — frequently asked
Is W-25Re stronger than EWTh-2?
Yes. W-25Re has a typical yield strength of 1,850 MPa (268 ksi) against 1,150 MPa (167 ksi) for EWTh-2 — about 61% more. Tensile strength is 2,100 MPa (305 ksi) vs 1,400 MPa (203 ksi).
Which is cheaper, EWTh-2 or W-25Re?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which welds better, EWTh-2 or W-25Re?
W-25Re. Its weldability rates fair (45/100) against not recommended (10/100) for EWTh-2.