Titanium Ti-8Al-1Mo-1V-DA vs Ti-8Al-1Mo-1V-STA
Titanium · Ti-8Al-1Mo-1V temper comparison
Ti-8Al-1Mo-1V-DA and Ti-8Al-1Mo-1V-STA are two conditions of the same titanium grade, Ti-8Al-1Mo-1V: DA (duplex Annealed) versus STA (solution treated and aged). The chemistry is identical, so every difference below comes from the condition. Ti-8Al-1Mo-1V-STA is the stronger of the two: yield strength 1,030 MPa (149 ksi) against 950 MPa (138 ksi) for Ti-8Al-1Mo-1V-DA, about 8% more; tensile strength follows at 1,100 MPa (160 ksi) vs 1,000 MPa (145 ksi). In exchange, Ti-8Al-1Mo-1V-DA is the more ductile: elongation 15% versus 11% for Ti-8Al-1Mo-1V-STA, and Ti-8Al-1Mo-1V-STA is harder (340 HB vs 315 HB).
Ti-8Al-1Mo-1V-DAChoose it when the part is bent, formed or impact-loaded.
Ti-8Al-1Mo-1V-STAChoose it when strength drives the design.
Ti-8Al-1Mo-1V-DA vs Ti-8Al-1Mo-1V-STA: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all titanium grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all titanium grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Ti-8Al-1Mo-1V-DATi-8Al-1Mo-1V-STA
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Hardness, Brinell
Hardness, Rockwell C
Same in both: Elastic (Young's) Modulus 124 GPa18 Msi · Shear Modulus 46 GPa6.7 Msi · Bulk Modulus 115 GPa16.7 Msi · Poisson's Ratio 0.32 · Compressive Strength 1,000 MPa145 ksi · Shear Strength 660 MPa95.7 ksi · Charpy V-Notch Impact (RT) 20 J14.8 ft·lbf · Hardness, Vickers 330 HV
Physical
Density and transition temperatures.
Same in both: Density 4.37 g/cm³0.16 lb/in³ · Melting Point (Solidus) 1,540°C2,804 °F · Liquidus Temperature 1,650°C3,002 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 6.5 W/m·K3.8 BTU/hr·ft·°F · Specific Heat Capacity 500 J/kg·K0.12 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 8.5 µm/m·K4.7 µin/in·°F · Latent Heat of Fusion 365 J/g157 BTU/lb · Min Service Temperature -100°C-148 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 0.9 % IACS · Electrical Resistivity 1.99×10⁻⁶ Ω·m78.3 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.1 V · Corrosion Resistance 85 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Same in both: Machinability Rating (AISI 1212 = 100 %) 20% · Weldability 55 / 100 · Formability (cold) 30 / 100 · Brazeability / Solderability 45 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 700 MJ/kg300,946 BTU/lb · Embodied Carbon (primary production) 45 kg CO₂/kg · Embodied Water 500 L/kg59.9 gal/lb · Typical Recycled Content 25%
Strength versus weight
Yield strength against density for every titanium grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Ti-8Al-1Mo-1V-DA vs Ti-8Al-1Mo-1V-STA — frequently asked
Is Ti-8Al-1Mo-1V-STA stronger than Ti-8Al-1Mo-1V-DA?
Yes. Ti-8Al-1Mo-1V-STA has a typical yield strength of 1,030 MPa (149 ksi) against 950 MPa (138 ksi) for Ti-8Al-1Mo-1V-DA — about 8% more. Tensile strength is 1,100 MPa (160 ksi) vs 1,000 MPa (145 ksi).
Which condition does FabDigit quote by default, DA or STA?
DA is the default Ti-8Al-1Mo-1V condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose Ti-8Al-1Mo-1V-DA over Ti-8Al-1Mo-1V-STA?
Pick Ti-8Al-1Mo-1V-DA when the part is bent, formed or impact-loaded. Pick Ti-8Al-1Mo-1V-STA when strength drives the design.
Ready to make it?
Upload a CAD file and FabDigit prices the part in Ti-8Al-1Mo-1V-DA and Ti-8Al-1Mo-1V-STA side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.