Titanium Ti-6Al-6V-2Sn As-Forged / Stress Relieved vs Ti-6Al-6V-2Sn-ST
Titanium · Ti-6Al-6V-2Sn temper comparison
Ti-6Al-6V-2Sn As-Forged / Stress Relieved and Ti-6Al-6V-2Sn-ST are two conditions of the same titanium grade, Ti-6Al-6V-2Sn: As-Forged / Stress Relieved versus ST (solution annealed). The chemistry is identical, so every difference below comes from the condition. Ti-6Al-6V-2Sn As-Forged / Stress Relieved is the stronger of the two: yield strength 990 MPa (144 ksi) against 900 MPa (131 ksi) for Ti-6Al-6V-2Sn-ST, about 10% more; tensile strength follows at 1,060 MPa (154 ksi) vs 1,000 MPa (145 ksi). In exchange, Ti-6Al-6V-2Sn-ST is the more ductile: elongation 16% versus 12% for Ti-6Al-6V-2Sn As-Forged / Stress Relieved, and Ti-6Al-6V-2Sn As-Forged / Stress Relieved is harder (345 HB vs 310 HB).
Ti-6Al-6V-2Sn As-Forged / Stress RelievedChoose it when strength drives the design.
Ti-6Al-6V-2Sn-STChoose it when the part is bent, formed or impact-loaded.
Ti-6Al-6V-2Sn As-Forged / Stress Relieved vs Ti-6Al-6V-2Sn-ST: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all titanium grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all titanium grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Ti-6Al-6V-2Sn As-Forged / Stress RelievedTi-6Al-6V-2Sn-ST
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 110 GPa16 Msi · Shear Modulus 42.5 GPa6.2 Msi · Bulk Modulus 105 GPa15.2 Msi · Poisson's Ratio 0.32
Physical
Density and transition temperatures.
Same in both: Density 4.54 g/cm³0.16 lb/in³ · Melting Point (Solidus) 1,690°C3,074 °F · Liquidus Temperature 1,705°C3,101 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 544 J/kg·K0.13 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 9.1 µm/m·K5.1 µin/in·°F · Latent Heat of Fusion 365 J/g157 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.1 V · Corrosion Resistance 82 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 30 / 100 · Brazeability / Solderability 45 / 100 · Polishability 65 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 690 MJ/kg296,647 BTU/lb · Embodied Carbon (primary production) 45 kg CO₂/kg · Embodied Water 900 L/kg108 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every titanium grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Ti-6Al-6V-2Sn As-Forged / Stress Relieved vs Ti-6Al-6V-2Sn-ST — frequently asked
Is Ti-6Al-6V-2Sn As-Forged / Stress Relieved stronger than Ti-6Al-6V-2Sn-ST?
Yes. Ti-6Al-6V-2Sn As-Forged / Stress Relieved has a typical yield strength of 990 MPa (144 ksi) against 900 MPa (131 ksi) for Ti-6Al-6V-2Sn-ST — about 10% more. Tensile strength is 1,060 MPa (154 ksi) vs 1,000 MPa (145 ksi).
Which condition does FabDigit quote by default, As-Forged / Stress Relieved or ST?
Annealed is the default Ti-6Al-6V-2Sn condition in the FabDigit quote flow (neither As-Forged / Stress Relieved nor ST). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which welds better, Ti-6Al-6V-2Sn As-Forged / Stress Relieved or Ti-6Al-6V-2Sn-ST?
Ti-6Al-6V-2Sn-ST. Its weldability rates fair (40/100) against poor (33/100) for Ti-6Al-6V-2Sn As-Forged / Stress Relieved.
Ready to make it?
Upload a CAD file and FabDigit prices the part in Ti-6Al-6V-2Sn As-Forged / Stress Relieved and Ti-6Al-6V-2Sn-ST side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.