Titanium IMI 550-ANN vs IMI 550-HR
Titanium · IMI 550 temper comparison
IMI 550-ANN and IMI 550-HR are two conditions of the same titanium grade, IMI 550: ANN (annealed) versus HR (hot rolled). The chemistry is identical, so every difference below comes from the condition. IMI 550-HR is the stronger of the two: yield strength 950 MPa (138 ksi) against 900 MPa (131 ksi) for IMI 550-ANN, about 6% more. In exchange, IMI 550-ANN is the more ductile: elongation 16% versus 12% for IMI 550-HR, and IMI 550-ANN is harder (333 HB vs 313 HB).
IMI 550-ANNChoose it when the part is bent, formed or impact-loaded.
IMI 550-HRChoose it when strength drives the design.
IMI 550-ANN vs IMI 550-HR: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all titanium grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all titanium grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Same in both: Shear Modulus 44 GPa6.4 Msi · Bulk Modulus 107 GPa15.5 Msi · Poisson's Ratio 0.32
Physical
Density and transition temperatures.
Same in both: Density 4.6 g/cm³0.17 lb/in³ · Melting Point (Solidus) 1,590°C2,894 °F · Liquidus Temperature 1,650°C3,002 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Same in both: Specific Heat Capacity 565 J/kg·K0.13 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 9.4 µm/m·K5.2 µin/in·°F · Latent Heat of Fusion 365 J/g157 BTU/lb · Max Service Temperature (continuous) 350°C662 °F · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 1.1 % IACS · Electrical Resistivity 1.65×10⁻⁶ Ω·m65 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.1 V · Corrosion Resistance 85 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 20 / 100 · Brazeability / Solderability 35 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 650 MJ/kg279,450 BTU/lb · Embodied Carbon (primary production) 42 kg CO₂/kg · Embodied Water 500 L/kg59.9 gal/lb · Typical Recycled Content 20%
Strength versus weight
Yield strength against density for every titanium grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
IMI 550-ANN vs IMI 550-HR — frequently asked
Is IMI 550-HR stronger than IMI 550-ANN?
Yes. IMI 550-HR has a typical yield strength of 950 MPa (138 ksi) against 900 MPa (131 ksi) for IMI 550-ANN — about 6% more. Tensile strength is 1,050 MPa (152 ksi) vs 1,000 MPa (145 ksi).
Which condition does FabDigit quote by default, ANN or HR?
STA is the default IMI 550 condition in the FabDigit quote flow (neither ANN nor HR). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which welds better, IMI 550-ANN or IMI 550-HR?
IMI 550-HR. Its weldability rates poor (30/100) against poor (25/100) for IMI 550-ANN.
Ready to make it?
Upload a CAD file and FabDigit prices the part in IMI 550-ANN and IMI 550-HR side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.