Titanium Grade 3 vs Ti Grade 4
Titanium · grade comparison
Titanium Grade 3 and Ti Grade 4 are both titanium grades. Ti Grade 4 is the stronger of the two: yield strength 520 MPa (75.4 ksi) against 420 MPa (60.9 ksi) for Grade 3, about 24% more; tensile strength follows at 620 MPa (89.9 ksi) vs 500 MPa (72.5 ksi). Ti Grade 4 is harder — 250 HB against 200 HB for Grade 3 — which matters for wear surfaces and threads. On the shop floor, Grade 3 forms better (good vs fair) and Ti Grade 4 sits in a lower cost tier (high, $$$$) than Grade 3 (specialty, $$$$$).
Ti Grade 4Choose it when strength drives the design, or when surface hardness matters.
Grade 3 vs Ti Grade 4: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all titanium grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all titanium grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Hardness, Rockwell C
Same in both: Shear Modulus 45 GPa6.5 Msi · Bulk Modulus 110 GPa16 Msi · Poisson's Ratio 0.34 · Elongation at Break 20% · Fracture Toughness (K_IC) 70 MPa·√m63.7 ksi·√in
Physical
Density and transition temperatures.
Liquidus Temperature
Same in both: Density 4.51 g/cm³0.16 lb/in³ · Melting Point (Solidus) 1,660°C3,020 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Latent Heat of Fusion
Min Service Temperature
Same in both: Thermal Expansion (CTE, 20–100 °C) 8.6 µm/m·K4.8 µin/in·°F · Max Service Temperature (continuous) 300°C572 °F
Electrical
Conductivity and insulation.
Electrical Resistivity
Same in both: Electrical Conductivity 3.1 % IACS
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.1 V · Corrosion Resistance 92 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Formability (cold)
Polishability
Same in both: Machinability Rating (AISI 1212 = 100 %) 28% · Weldability 85 / 100 · Castability 35 / 100 · Brazeability / Solderability 40 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Shock Resistance Index
Same in both: Thermal Diffusivity 7 mm²/s
Strength versus weight
Yield strength against density for every titanium grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | Grade 3 | Ti Grade 4 |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Default condition | O | — |
| Relative cost | $$$$$ Specialty | $$$$ High |
| Min. machined wall | 1 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| AlCrN | Yes | — |
| AlTiN | Yes | — |
| Anodizing Type II | Yes | — |
| CVD Al2O3 | Yes | — |
| CVD TiCN | Yes | — |
| CVD TiN | Yes | — |
| Cerakote | Yes | — |
| CrN | Yes | — |
| DLC | Yes | — |
| Electropolishing | Yes | — |
| HVOF Coating | Yes | — |
| MoS2 | Yes | — |
| Multilayer CVD | Yes | — |
| TiAlN | Yes | — |
| TiB2 | Yes | — |
| TiCN | Yes | — |
| TiN | Yes | — |
| WC/C | Yes | — |
They share 1 finish: Plasma Spray.
Grade 3 vs Ti Grade 4 — frequently asked
Is Ti Grade 4 stronger than Grade 3?
Yes. Ti Grade 4 has a typical yield strength of 520 MPa (75.4 ksi) against 420 MPa (60.9 ksi) for Grade 3 — about 24% more. Tensile strength is 620 MPa (89.9 ksi) vs 500 MPa (72.5 ksi).
Which is cheaper, Grade 3 or Ti Grade 4?
Ti Grade 4 is the lower-cost material: it sits in the high tier ($$$$) while Grade 3 is specialty ($$$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, Grade 3 or Ti Grade 4?
Grade 3. Its machinability rates fair (35/100) against poor (30/100) for Ti Grade 4.
Ready to make it?
Upload a CAD file and FabDigit prices the part in Grade 3 and Ti Grade 4 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.