Titanium Grade 3 vs Ti Grade 17
Titanium · grade comparison
Titanium Grade 3 and Ti Grade 17 are both titanium grades. Grade 3 is the stronger of the two: yield strength 420 MPa (60.9 ksi) against 230 MPa (33.4 ksi) for Ti Grade 17, about 83% more; tensile strength follows at 500 MPa (72.5 ksi) vs 330 MPa (47.9 ksi). In exchange, Ti Grade 17 is the more ductile: elongation 32% versus 20% for Grade 3, and Grade 3 is harder (200 HB vs 120 HB). On the shop floor, Ti Grade 17 sits in a lower cost tier (high, $$$$) than Grade 3 (specialty, $$$$$).
Grade 3Choose it when strength drives the design.
Ti Grade 17Choose it when the part is bent, formed or impact-loaded, or when cost is the deciding factor.
Grade 3 vs Ti Grade 17: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all titanium grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all titanium grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 103 GPa14.9 Msi · Shear Modulus 45 GPa6.5 Msi · Poisson's Ratio 0.34
Physical
Density and transition temperatures.
Liquidus Temperature
Same in both: Density 4.51 g/cm³0.16 lb/in³ · Melting Point (Solidus) 1,660°C3,020 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Latent Heat of Fusion
Min Service Temperature
Same in both: Specific Heat Capacity 523 J/kg·K0.12 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 8.6 µm/m·K4.8 µin/in·°F · Max Service Temperature (continuous) 300°C572 °F
Electrical
Conductivity and insulation.
Electrical Resistivity
Same in both: Electrical Conductivity 3.1 % IACS
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.1 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Same in both: Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Same in both: Typical Recycled Content 25%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Same in both: Specific Stiffness (E / density) 22.8 MN·m/kg
Strength versus weight
Yield strength against density for every titanium grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | Grade 3 | Ti Grade 17 |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Default condition | O | — |
| Relative cost | $$$$$ Specialty | $$$$ High |
| Min. machined wall | 1 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| AlCrN | Yes | — |
| AlTiN | Yes | — |
| Anodizing Type II | Yes | — |
| CVD Al2O3 | Yes | — |
| CVD TiCN | Yes | — |
| CVD TiN | Yes | — |
| Cerakote | Yes | — |
| CrN | Yes | — |
| DLC | Yes | — |
| Electropolishing | Yes | — |
| HVOF Coating | Yes | — |
| MoS2 | Yes | — |
| Multilayer CVD | Yes | — |
| TiAlN | Yes | — |
| TiB2 | Yes | — |
| TiCN | Yes | — |
| TiN | Yes | — |
| WC/C | Yes | — |
They share 1 finish: Plasma Spray.
Grade 3 vs Ti Grade 17 — frequently asked
Is Grade 3 stronger than Ti Grade 17?
Yes. Grade 3 has a typical yield strength of 420 MPa (60.9 ksi) against 230 MPa (33.4 ksi) for Ti Grade 17 — about 83% more. Tensile strength is 500 MPa (72.5 ksi) vs 330 MPa (47.9 ksi).
Which is cheaper, Grade 3 or Ti Grade 17?
Ti Grade 17 is the lower-cost material: it sits in the high tier ($$$$) while Grade 3 is specialty ($$$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
When should I choose Grade 3 over Ti Grade 17?
Pick Grade 3 when strength drives the design. Pick Ti Grade 17 when the part is bent, formed or impact-loaded, or when cost is the deciding factor.
Ready to make it?
Upload a CAD file and FabDigit prices the part in Grade 3 and Ti Grade 17 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.