Titanium Grade 2H CW-SR vs Grade 2H-HR
Titanium · Grade 2H temper comparison
Grade 2H CW-SR and Grade 2H-HR are two conditions of the same titanium grade, Grade 2H: CW-SR (cold worked and stress relieved) versus HR (hot rolled). The chemistry is identical, so every difference below comes from the condition. Grade 2H CW-SR is the stronger of the two: yield strength 470 MPa (68.2 ksi) against 385 MPa (55.8 ksi) for Grade 2H-HR, about 22% more; tensile strength follows at 560 MPa (81.2 ksi) vs 490 MPa (71.1 ksi). In exchange, Grade 2H-HR is the more ductile: elongation 22% versus 15% for Grade 2H CW-SR, and Grade 2H CW-SR is harder (205 HB vs 175 HB). Grade 2H-HR runs hotter in service (300°C vs 250°C continuous).
Grade 2H CW-SRChoose it when strength drives the design.
Grade 2H-HRChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
Grade 2H CW-SR vs Grade 2H-HR: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all titanium grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all titanium grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 105 GPa15.2 Msi · Shear Modulus 45 GPa6.5 Msi · Bulk Modulus 110 GPa16 Msi · Poisson's Ratio 0.34
Physical
Density and transition temperatures.
Same in both: Density 4.51 g/cm³0.16 lb/in³ · Melting Point (Solidus) 1,665°C3,029 °F · Liquidus Temperature 1,670°C3,038 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 16.4 W/m·K9.5 BTU/hr·ft·°F · Specific Heat Capacity 523 J/kg·K0.12 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 8.6 µm/m·K4.8 µin/in·°F · Latent Heat of Fusion 295 J/g127 BTU/lb · Min Service Temperature -250°C-418 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 3.1 % IACS · Electrical Resistivity 5.6×10⁻⁷ Ω·m22 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.1 V · Corrosion Resistance 92 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Weldability 85 / 100 · Castability 25 / 100 · Brazeability / Solderability 40 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 675 MJ/kg290,198 BTU/lb · Embodied Carbon (primary production) 44 kg CO₂/kg · Embodied Water 700 L/kg83.9 gal/lb · Typical Recycled Content 25%
Strength versus weight
Yield strength against density for every titanium grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Grade 2H CW-SR vs Grade 2H-HR — frequently asked
Is Grade 2H CW-SR stronger than Grade 2H-HR?
Yes. Grade 2H CW-SR has a typical yield strength of 470 MPa (68.2 ksi) against 385 MPa (55.8 ksi) for Grade 2H-HR — about 22% more. Tensile strength is 560 MPa (81.2 ksi) vs 490 MPa (71.1 ksi).
Which condition does FabDigit quote by default, CW-SR or HR?
ANN is the default Grade 2H condition in the FabDigit quote flow (neither CW-SR nor HR). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose Grade 2H CW-SR over Grade 2H-HR?
Pick Grade 2H CW-SR when strength drives the design. Pick Grade 2H-HR when the part is bent, formed or impact-loaded, or when the part sees heat.