Titanium Grade 23 vs Ti-6Al-2Sn-4Zr-6Mo
Titanium · grade comparison
Titanium Grade 23 and Ti-6Al-2Sn-4Zr-6Mo are both titanium grades. Ti-6Al-2Sn-4Zr-6Mo is the stronger of the two: yield strength 1,100 MPa (160 ksi) against 850 MPa (123 ksi) for Grade 23, about 29% more; tensile strength follows at 1,170 MPa (170 ksi) vs 930 MPa (135 ksi). In exchange, Grade 23 is the more ductile: elongation 15% versus 10% for Ti-6Al-2Sn-4Zr-6Mo, and Ti-6Al-2Sn-4Zr-6Mo is harder (350 HB vs 320 HB). Grade 23 is lighter (4.43 g/cm³ vs 4.65 g/cm³ for Ti-6Al-2Sn-4Zr-6Mo) and Ti-6Al-2Sn-4Zr-6Mo runs hotter in service (400°C vs 350°C continuous). On the shop floor, Grade 23 welds better (very good vs poor).
Grade 23Choose it when the part is bent, formed or impact-loaded, or when weight is the constraint.
Ti-6Al-2Sn-4Zr-6MoChoose it when strength drives the design, or when the part sees heat.
Grade 23 vs Ti-6Al-2Sn-4Zr-6Mo: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all titanium grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all titanium grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Latent Heat of Fusion 365 J/g157 BTU/lb
Electrical
Conductivity and insulation.
Electrical Resistivity
Same in both: Electrical Conductivity 1 % IACS
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.1 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Polishability
Same in both: Brazeability / Solderability 35 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Same in both: Embodied Energy (primary production) 700 MJ/kg300,946 BTU/lb
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every titanium grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | Grade 23 | Ti-6Al-2Sn-4Zr-6Mo |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| 3D printing | Yes | — |
| Default condition | O | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | 1 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| AlCrN | Yes | — |
| AlTiN | Yes | — |
| Anodizing Type II | Yes | — |
| CVD Al2O3 | Yes | — |
| CVD TiCN | Yes | — |
| CVD TiN | Yes | — |
| Cerakote | Yes | — |
| CrN | Yes | — |
| DLC | Yes | — |
| Electropolishing | Yes | — |
| HVOF Coating | Yes | — |
| MoS2 | Yes | — |
| Multilayer CVD | Yes | — |
| TiAlN | Yes | — |
| TiB2 | Yes | — |
| TiCN | Yes | — |
| TiN | Yes | — |
| WC/C | Yes | — |
They share 1 finish: Plasma Spray.
Grade 23 vs Ti-6Al-2Sn-4Zr-6Mo — frequently asked
Is Ti-6Al-2Sn-4Zr-6Mo stronger than Grade 23?
Yes. Ti-6Al-2Sn-4Zr-6Mo has a typical yield strength of 1,100 MPa (160 ksi) against 850 MPa (123 ksi) for Grade 23 — about 29% more. Tensile strength is 1,170 MPa (170 ksi) vs 930 MPa (135 ksi).
Which is cheaper, Grade 23 or Ti-6Al-2Sn-4Zr-6Mo?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, Grade 23 or Ti-6Al-2Sn-4Zr-6Mo?
Grade 23. Its machinability rates poor (20/100) against not recommended (14/100) for Ti-6Al-2Sn-4Zr-6Mo; for welding the order is Grade 23 first (very good, 80/100) then Ti-6Al-2Sn-4Zr-6Mo (poor, 30/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in Grade 23 and Ti-6Al-2Sn-4Zr-6Mo side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.