Titanium Grade 23 vs TC11
Titanium · grade comparison
Titanium Grade 23 and TC11 are both titanium grades. TC11 is the stronger of the two: yield strength 960 MPa (139 ksi) against 850 MPa (123 ksi) for Grade 23, about 13% more; tensile strength follows at 1,080 MPa (157 ksi) vs 930 MPa (135 ksi). In exchange, Grade 23 is the more ductile: elongation 15% versus 13% for TC11. TC11 runs hotter in service (500°C vs 350°C continuous) and TC11 conducts heat better (7.9 W/m·K vs 6.7 W/m·K). On the shop floor, Grade 23 welds better (very good vs fair).
Grade 23Choose it when the part is bent, formed or impact-loaded, or when it will be welded.
TC11Choose it when strength drives the design, or when the part sees heat.
Grade 23 vs TC11: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all titanium grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all titanium grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Same in both: Shear Modulus 44 GPa6.4 Msi
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Same in both: Liquidus Temperature 1,660°C3,020 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Latent Heat of Fusion
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Thermal Expansion (CTE, 20–100 °C) 8.6 µm/m·K4.8 µin/in·°F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.1 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Shock Resistance Index
Same in both: Thermal Diffusivity 2.9 mm²/s
Strength versus weight
Yield strength against density for every titanium grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | Grade 23 | TC11 |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| 3D printing | Yes | — |
| Default condition | O | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | 1 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| AlCrN | Yes | — |
| AlTiN | Yes | — |
| Anodizing Type II | Yes | — |
| CVD Al2O3 | Yes | — |
| CVD TiCN | Yes | — |
| CVD TiN | Yes | — |
| Cerakote | Yes | — |
| CrN | Yes | — |
| DLC | Yes | — |
| Electropolishing | Yes | — |
| HVOF Coating | Yes | — |
| MoS2 | Yes | — |
| Multilayer CVD | Yes | — |
| TiAlN | Yes | — |
| TiB2 | Yes | — |
| TiCN | Yes | — |
| TiN | Yes | — |
| WC/C | Yes | — |
They share 1 finish: Plasma Spray.
Grade 23 vs TC11 — frequently asked
Is TC11 stronger than Grade 23?
Yes. TC11 has a typical yield strength of 960 MPa (139 ksi) against 850 MPa (123 ksi) for Grade 23 — about 13% more. Tensile strength is 1,080 MPa (157 ksi) vs 930 MPa (135 ksi).
Which is cheaper, Grade 23 or TC11?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, Grade 23 or TC11?
Grade 23, by a small margin. Both rate poor for machinability — 20/100 against 15/100 for TC11; for welding the order is Grade 23 first (very good, 80/100) then TC11 (fair, 45/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in Grade 23 and TC11 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.