Titanium Grade 17 vs Ti-6Al-2Nb-1Ta-0.8Mo
Titanium · grade comparison
Titanium Grade 17 and Ti-6Al-2Nb-1Ta-0.8Mo are both titanium grades. Ti-6Al-2Nb-1Ta-0.8Mo is the stronger of the two: yield strength 780 MPa (113 ksi) against 240 MPa (34.8 ksi) for Grade 17, about 3.3 times as much; tensile strength follows at 860 MPa (125 ksi) vs 330 MPa (47.9 ksi). In exchange, Grade 17 is the more ductile: elongation 32% versus 15% for Ti-6Al-2Nb-1Ta-0.8Mo, and Ti-6Al-2Nb-1Ta-0.8Mo is harder (285 HB vs 120 HB). Ti-6Al-2Nb-1Ta-0.8Mo is stiffer (114 GPa vs 103 GPa) and Ti-6Al-2Nb-1Ta-0.8Mo runs hotter in service (400°C vs 315°C continuous). On the shop floor, Grade 17 machines more easily (fair vs poor).
Grade 17Choose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
Ti-6Al-2Nb-1Ta-0.8MoChoose it when strength drives the design, or when the part sees heat.
Grade 17 vs Ti-6Al-2Nb-1Ta-0.8Mo: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all titanium grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all titanium grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Hardness, Rockwell C
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Latent Heat of Fusion
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Thermal Expansion (CTE, 20–100 °C) 8.6 µm/m·K4.8 µin/in·°F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.1 V · Corrosion Resistance 95 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Brazeability / Solderability
Castability
Same in both: Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Water
Same in both: Embodied Carbon (primary production) 42 kg CO₂/kg · Typical Recycled Content 25%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every titanium grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | Grade 17 | Ti-6Al-2Nb-1Ta-0.8Mo |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Both take the same 1 finish: Plasma Spray.
Grade 17 vs Ti-6Al-2Nb-1Ta-0.8Mo — frequently asked
Is Ti-6Al-2Nb-1Ta-0.8Mo stronger than Grade 17?
Yes. Ti-6Al-2Nb-1Ta-0.8Mo has a typical yield strength of 780 MPa (113 ksi) against 240 MPa (34.8 ksi) for Grade 17 — about 3.3 times as much. Tensile strength is 860 MPa (125 ksi) vs 330 MPa (47.9 ksi).
Which is cheaper, Grade 17 or Ti-6Al-2Nb-1Ta-0.8Mo?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, Grade 17 or Ti-6Al-2Nb-1Ta-0.8Mo?
Grade 17. Its machinability rates fair (40/100) against poor (18/100) for Ti-6Al-2Nb-1Ta-0.8Mo; for welding the order is Grade 17 first (excellent, 88/100) then Ti-6Al-2Nb-1Ta-0.8Mo (very good, 80/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in Grade 17 and Ti-6Al-2Nb-1Ta-0.8Mo side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.