Steel WCC N+T vs WCC Q&T
Steel · WCC temper comparison
WCC N+T and WCC Q&T are two conditions of the same steel grade, WCC: N+T (normalized and tempered) versus Q&T (quenched and tempered). The chemistry is identical, so every difference below comes from the condition. WCC Q&T is the stronger of the two: yield strength 380 MPa (55.1 ksi) against 315 MPa (45.7 ksi) for WCC N+T, about 21% more; tensile strength follows at 585 MPa (84.8 ksi) vs 540 MPa (78.3 ksi). WCC Q&T is harder — 197 HB against 180 HB for WCC N+T — which matters for wear surfaces and threads.
WCC Q&TChoose it when strength drives the design, or when surface hardness matters.
WCC N+T vs WCC Q&T: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Same in both: Elastic (Young's) Modulus 200 GPa29 Msi · Shear Modulus 78 GPa11.3 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Compressive Strength 315 MPa45.7 ksi · Shear Strength 345 MPa50 ksi · Fracture Toughness (K_IC) 90 MPa·√m81.9 ksi·√in · Hardness, Vickers 190 HV
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,425°C2,597 °F · Liquidus Temperature 1,505°C2,741 °F
Thermal
How each material carries heat and how hot it can run.
Min Service Temperature
Same in both: Thermal Conductivity 48 W/m·K27.7 BTU/hr·ft·°F · Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12 µm/m·K6.7 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Max Service Temperature (continuous) 425°C797 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 9.5 % IACS · Electrical Resistivity 1.8×10⁻⁷ Ω·m7.09 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.62 V · Corrosion Resistance 12 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability Rating (AISI 1212 = 100 %)
Same in both: Machinability 58 / 100 · Weldability 72 / 100 · Formability (cold) 20 / 100 · Castability 78 / 100 · Brazeability / Solderability 60 / 100 · Polishability 45 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 27 MJ/kg11,608 BTU/lb · Embodied Carbon (primary production) 2.2 kg CO₂/kg · Embodied Water 45 L/kg5.4 gal/lb · Typical Recycled Content 85%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
WCC N+T vs WCC Q&T — frequently asked
Is WCC Q&T stronger than WCC N+T?
Yes. WCC Q&T has a typical yield strength of 380 MPa (55.1 ksi) against 315 MPa (45.7 ksi) for WCC N+T — about 21% more. Tensile strength is 585 MPa (84.8 ksi) vs 540 MPa (78.3 ksi).
Which condition does FabDigit quote by default, N+T or Q&T?
N+T is the default WCC condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose WCC N+T over WCC Q&T?
Pick WCC Q&T when strength drives the design, or when surface hardness matters.